Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 10% Cold Work
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | INCONEL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed + 10% Cold Work.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Tensile strength (ultimate and yield), elongation, and reduction of area values are for annealed then cold worked samples. This produces ASTM grain size 9.0. Other property values are typical of this alloy.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.44 g/cc | 0.305 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 915.6 MPa | 132800 psi | |
| Tensile Strength, Yield | 462 MPa @Strain 0.200 % |
67000 psi @Strain 0.200 % |
|
| Elongation at Break | 48 % | 48 % | |
| Modulus of Elasticity | 208 GPa | 30200 ksi | |
| Poissons Ratio | 0.28 | 0.28 | |
| Shear Modulus | 81.4 GPa | 11800 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.8 µm/m-°C @Temperature 21.0 - 100 °C |
7.11 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
| 13.3 µm/m-°C @Temperature 21.0 - 300 °C |
7.39 µin/in-°F @Temperature 69.8 - 572 °F |
Mean | |
| 13.9 µm/m-°C @Temperature 21.0 - 500 °C |
7.72 µin/in-°F @Temperature 69.8 - 932 °F |
Mean | |
| 14.9 µm/m-°C @Temperature 21.0 - 700 °C |
8.28 µin/in-°F @Temperature 69.8 - 1290 °F |
Mean | |
| Specific Heat Capacity | 0.410 J/g-°C | 0.0980 BTU/lb-°F | |
| Thermal Conductivity | 9.70 W/m-K | 67.3 BTU-in/hr-ft²-°F | |
| Melting Point | 1290 - 1350 °C | 2350 - 2460 °F | |
| Solidus | 1290 °C | 2350 °F | |
| Liquidus | 1350 °C | 2460 °F | |
| Maximum Service Temperature, Air | 650 °C | 1200 °F | resistance to low cycle and thermal fatigue |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | <= 0.40 % | <= 0.40 % | |
| Carbon, C | <= 0.030 % | <= 0.030 % | |
| Chromium, Cr | 20 - 23 % | 20 - 23 % | |
| Cobalt, Co | <= 1.0 % | <= 1.0 % | |
| Iron, Fe | <= 5.0 % | <= 5.0 % | |
| Manganese, Mn | <= 0.50 % | <= 0.50 % | |
| Molybdenum, Mo | 8.0 - 10 % | 8.0 - 10 % | |
| Nickel, Ni | >= 58 % | >= 58 % | |
| Niobium, Nb (Columbium, Cb) | 3.15 - 4.15 % | 3.15 - 4.15 % | Includes Ta |
| Nitrogen, N | <= 0.020 % | <= 0.020 % | |
| Phosphorous, P | <= 0.015 % | <= 0.015 % | |
| Silicon, Si | <= 0.020 % | <= 0.020 % | |
| Sulfur, S | <= 0.015 % | <= 0.015 % | |
| Titanium, Ti | <= 0.40 % | <= 0.40 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000132 ohm-cm | 0.000132 ohm-cm | |
| Magnetic Permeability | 1.0006 | 1.0006 | at 200 Oersted (15.9 kA/m) |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPHC T5040 Polypropylene, Mineral Reinforced
- Micropol Microlink XL Crosslinkable Polyethylene
- Lucite International Colacryl ® PD2 Acrylic Dental Resin
- Teknor Apex APEX® 90-A471R-75-NT Polyvinyl Chloride, Flexible
- SABIC Innovative Plastics LNP THERMOCOMP QF004 PA 6/10 (Asia Pacific)
- Arlon 55146R030 0.030" (0.762 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- ACC Silcoset 101 Low Tear Condensation Cure 2-Part Molding Rubber
- SABIC Innovative Plastics LNP Verton RV004ESV_GY7E070 PA 66
- Lucas-Milhaupt BRAZE 580 Silver Based Cadmium Free Filler Metal
Copyright © lookpolymers.com All Rights Reserved