Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 20.0 - 25.0 µm/m-°C @Temperature 50.0 - 150 °C |
11.1 - 13.9 µin/in-°F @Temperature 122 - 302 °F |
ISO 11359-2 |
Raschig Group DECAL® 666/8 Phenolic Glass-fiber reinforced phenolic molding compound with mineral fillers. High heat resistance, reduced mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This prod.. |
|||
CTE, linear, Parallel to Flow | 20.0 - 25.0 µm/m-°C @Temperature 50.0 - 150 °C |
11.1 - 13.9 µin/in-°F @Temperature 122 - 302 °F |
ISO 11359-2 |
Raschig Group EPOXIDUR® 3581 S ZC EP Epoxy Molding Compound Inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures. Very good sealing connection on .. |
|||
CTE, linear, Parallel to Flow | 15.0 - 25.0 µm/m-°C @Temperature 50.0 - 100 °C |
8.33 - 13.9 µin/in-°F @Temperature 122 - 212 °F |
ISO 11359-2 |
Raschig Group RALUPOL® 2200 UP Polyester Organically filled polyester molding compound. Low post-shrinkage, good electrical values and mechanical properties, high surface quality and good color stability (non-yellowing). This product meets.. |
|||
CTE, linear, Parallel to Flow | 15.0 - 25.0 µm/m-°C @Temperature 20.0 °C |
8.33 - 13.9 µin/in-°F @Temperature 68.0 °F |
TMA |
Vyncolit X658 Novolac Phenolic Glass fiber and mineral filled phenolic molding compound with excellent mechanical and thermal properties and a very good dimensional stability.USES: Complex precision parts.Information provided by .. |
|||
CTE, linear, Parallel to Flow | 20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 11359-1/-2 |
BASF Ultramid® B3EG5 25% Glass Filled PA6 (Dry) Description: 25% glass-fiber reinforced injection-molding grade for industrial articles and electrical insulating partsInformation provided by BASF |
|||
CTE, linear, Parallel to Flow | 20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
BASF Ultramid® B3EG6 30% Glass Filled PA6 (Dry) Ultramid B3EG6 is a 30% glass fiber reinforced injection molding PA6 grade. It conforms to FDA requirements of 21 CFR 177.1500. |
|||
CTE, linear, Parallel to Flow | 20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
BASF Ultramid® B3EG6 BK00564 30% Glass Filled PA6 (Dry) Ultramid B3EG6 BK00564 is a 30% glass fiber reinforced, pigmented black injection molding PA6 grade. It conforms to FDA requirements of 21 CFR 177.1500. |
|||
CTE, linear, Parallel to Flow | 20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
BASF Ultramid® B3EG6 LS BK 23189 30% Glass Filled PA6 (Dry) Information provided by BASF |
|||
CTE, linear, Parallel to Flow | 20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
BASF Ultramid® B3ZG6 30% Glass Filled PA6 (Dry) Ultramid B3ZG6 is an impact-modified, 30% glass fiber reinforced injection molding PA6 grade for industrial items having very high impact strength and rigidity. |
|||
CTE, linear, Parallel to Flow | 20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
BASF Ultramid® B3ZG6 BK30564 30% Glass Filled PA6 (Dry) Ultramid B3ZG6 BK30564 is an impact-modified, pigmented black, 30% glass fiber reinforced injection molding PA6 grade for industrial items having very high impact strength and rigidity. |
|||
CTE, linear, Parallel to Flow | 20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 11359-1/-2 |
BASF Ultramid® B3WG5 25% Glass Filled PA6 (Dry) Description: 25% glass-fiber reinforced and heat aging resistant injection-molding grade, for instance, for fan impeller glass-fiber reinforced injection-molding grade for industrial articles and el.. |
|||
CTE, linear, Parallel to Flow | 20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 11359-1/-2 |
BASF Ultramid® B3WG5 BK 00654 PA6 25% Glass Filled BK (Dry) Description: 25% glass-fiber reinforced and heat aging resistant injection-molding grade, for instance, for fan impeller glass-fiber reinforced injection-molding grade for industrial articles and el.. |
|||
CTE, linear, Parallel to Flow | 20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
BASF Ultramid® B3WG6 30% Glass Filled PA6 (Dry) Ultramid B3WG6 is a 30% glass fiber reinforced, heat stabilized injection molding PA6 grade. |
|||
CTE, linear, Parallel to Flow | 20.0 - 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 - 13.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-1/-2 |
BASF Ultramid® B3WG6 BK00564 30% Glass Filled PA6 (Dry) Ultramid B3WG6 BK00564 is a 30% glass fiber reinforced, pigmented black, heat stabilized injection molding PA6 grade. |