Thermal Properties | Metric | English | Comments |
---|---|---|---|
Vicat Softening Point | 50.0 °C | 122 °F | Rate A; ISO 306/A50 |
Premix Thermoplastics PRE-ELEC® CP 1316
(discontinued **) PRE-ELEC CP 1316 is a conductive thermoplastic compound based on a polyolefin copolymer. Conductivity is achieved by using special conductive carbon black. In addition to a very low electrical resis.. |
|||
Vicat Softening Point | 50.0 °C | 122 °F | ASTM D1525 |
DuPont Nucrel® 2906 Ethylene-Methacrylic Acid Copolymer Resin
(discontinued **) Nucrel® 2906 is a tough, lightweight, easily processed ethylene copolymer resin. This resin is inherently flexible without the need for plasticizers. The resin can be pigmented, UV-stabilized for.. |
|||
Vicat Softening Point | 50.0 °C | 122 °F | 1000g; ASTM D-1525 |
ExxonMobil Optema® TC-113 Ethylene Methyl Acrylate for Compounding
(discontinued **) Data provided by the manufacturer, Exxon Chemical.23.5% Methyl Acrylate. An Ethylene Methyl Acrylate copolymer which can be used as an impact modifier or compatibilizer in polymer compounds. It ca.. |
|||
Vicat Softening Point | 50.0 °C | 122 °F | Rate A; ASTM D1525 |
Covestro Texin® DP7-3006 Thermoplastic Polyurethane, Polyether-based, Aliphatic
(discontinued **) Information provided by Bayer Corporation, Plastics DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and has officially adopted its new name – Covestro. This produ.. |
|||
Vicat Softening Point | 50.0 °C | 122 °F | ASTM D1525 |
DuPont Bynel® 21E553 Adhesive Resin
(discontinued **) Bynel® Series 2100 resins are anhydride-modified ethylene acrylate resins. They contain a temperature stable ester that makes them functional in high temperature coextrusions. They are available in.. |
|||
Vicat Softening Point | 50.0 °C | 122 °F | |
Lucite International Elvacite ® 4400 Acrylic Resin Elvacite® 4400 is a solid methacrylate copolymer bead resin designed for use in formulating thermosetting powder coating systems for exceptionally durable films. The resin may be used as the main.. |
|||
Vicat Softening Point | 50.0 °C | 122 °F | ASTM D1525 |
Solvay Specialty Polymers Polidan® PNT 0856/35 Polyethylene, Crosslinked (XLPE) POLIDAN® PNT 0856/35 is a silane crosslinkable PE compound which is used together with a catalyst masterbatch to accelerate the crosslinking reaction.Features: Crosslinkable; Good Flexibility; Lo.. |
|||
Vicat Softening Point | 50.0 °C | 122 °F | ASTM D1525 |
Westlake EMAC® Plus SP1305 20% Ethylene-Methyl Acrylate Copolymer Westlake EMAC® Plus SP1305 is a 20% EMA copolymer designed for blown or cast film, tie-layers, and extrusions where flexibility, compatibility, or low heat seal temperatures are required. SP1305 is.. |
|||
Vicat Softening Point | 50.0 °C | 122 °F | ASTM D1525 |
Westlake EMAC® SP2260 24% Ethylene-Methyl Acrylate Copolymer Westlake EMAC® SP2260 is a 24% EMA copolymer designed for blown or cast film, tie-layers, and extrusions where flexibility, compatibility, or low heat seal temperatures are required. SP2260 provide.. |
|||
Vicat Softening Point | 50.0 °C | 122 °F | ASTM-D1525 |
Westlake EMAC® SP2409 20% EMA Copolymer Westlake EMAC� SP2409 is a 20% EMA copolymer designed for extrusion coating, tie-layers, and extrusions where flexibility, compatibility, low heat seal temperatures, or a high coefficient of fr.. |
|||
Vicat Softening Point | 50.0 °C | 122 °F | ASTM D1525 |
DuPont Bynel® 1123 Modified EVA Adhesive Resin Bynel® Series 1100 resins are modified ethylene vinyl acetate polymers. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyethylen.. |
|||
Vicat Softening Point | >= 50.0 °C @Load 5.00 kg |
>= 122 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
Cossa Polimeri ESTAPROP KUR 1010 TG05 Polypropylene, 5% Mineral Filled PP copolymer 5% mineral fillerElastomer modified, very high impact strength at low temperatureInformation provided by Cossa Polimeri S.r.l. |
|||
Vicat Softening Point | 50.0 °C | 122 °F | 50°C/h 50N; ISO 306 |
DSM Arnitel® EM460 46 Shore D, Injection Molding or Extrusion Grade Copolyester Elastomer (North America) Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arn.. |
|||
Vicat Softening Point | 50.0 °C | 122 °F | 50°C/h 50N; ISO 306 |
DSM Arnitel® EM460 Polyether Ester Elastomer (European and Asian Grade) Product description: Arnitel® combines the advantages of engineering thermoplastics, being easy to process with excellent mechanical properties, at the same time with the flexibility of rubbers.Arn.. |
|||
Vicat Softening Point | 50.0 °C | 122 °F | ASTM D1525 and ISO 306/A |
ExxonMobil Exact™ 9371 Ethylene-based Plastomer Resin Product Description: Exact 9371 plastomer is an ethylene butene copolymer produced using ExxonMobil Chemical's EXXPOL™ Technology, exhibiting both plastic and elastomeric properties.Key Features:P.. |
|||
Vicat Softening Point | 50.0 °C | 122 °F | ASTM D1525, ISO 306 |
DuPont™ Bynel® 21E533 Anhydride Modified Ethylene Acrylate BYNEL® Series 2100 resins are anhydride modified ethylene acrylate resins. They contain a temperature stable ester which makes them functional in high temperature coextrusions. They are available i.. |
|||
Vicat Softening Point | 50.0 °C | 122 °F | ASTM D1525, ISO 306 |
DuPont™ Elvax® 3178Z Ethylene Vinyl Acetate DuPont™ Elvax® 3178Z is an extrudable ethylene-vinyl acetate copolymer resin available in pellet form for use in conventional extrusion equipment designed to process polyethylene resins. ELVAX® 3.. |
|||
Vicat Softening Point | 50.0 °C | 122 °F | ASTM D1525 |
ExxonMobil Polybilt™ Bitumen Modifier 106 Low Density Polyethylene Resin Polybilt 106 is compatible with a large variety of bitumens. For optimum results are preliminary study is recommended to determine the base bitumen grade and optimum Polybilt 106 content to achieve .. |
|||
Vicat Softening Point | >= 50.0 °C @Load 5.00 kg |
>= 122 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
Cossa Polimeri ESTAPROP KUR 1520 TG05 Polypropylene, 10% Mineral Filled PP copolymer 10% mineral fillerElastomer modified, very high impact strength at low temperatureInformation provided by Cossa Polimeri S.r.l. |
|||
Vicat Softening Point | 50.0 °C | 122 °F | ASTM D1525-82 |
Arkema Group Orevac® 18216 Maleic Anhydride modified EVA Orevac® 18216 resin is a maleic anhydride modified ethylene - vinyl acetate copolymer designed for the coextrusion of multilayer barrier structures providing outstanding adhesion between layers.Inf.. |
|||
Vicat Softening Point | 50.0 °C | 122 °F | 50°C/hr; 50N |
Arkema Group Appryl® 7280 Polypropylene - Polyethylene Copolymer PP/PE copolymer colored directly or during the injection molding process. This grade with a very good impact test at low temperature, has been developed for bumpers applications for the automotive i.. |
|||
Vicat Softening Point | 50.0 - 210 °C | 122 - 410 °F | Average value: 145 °C Grade Count:55 |
Overview of materials for Polyether Ester Elastomer This property data is a summary of similar materials in the MatWeb database for the category "Polyether Ester Elastomer". Each property range of values reported is minimum and maximum values of appr.. |
|||
Vicat Softening Point | 50.0 - 155 °C | 122 - 311 °F | Average value: 112 °C Grade Count:25 |
Overview of materials for Polypropylene with 10% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 10% Talc Filler". Specific grades with primary filler content between 5% and 14% are .. |
|||
Vicat Softening Point | 50.0 °C @Load 5.00 kg |
122 °F @Load 11.0 lb |
|
LATI Latimass 53/11-02 D030 PP Homopolymer, Impact Modified Specific density compound based on Polypropylene homopolymer (PPh), impact modified. Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation.. |
|||
Vicat Softening Point | 50.0 °C @Load 5.00 kg |
122 °F @Load 11.0 lb |
|
LATI Latimass 53-04 D008 PP Homopolymer, Impact Modified Specific density compound based on Polypropylene homopolymer (PPh), impact modified. Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation.. |
|||
Vicat Softening Point | 50.0 °C @Load 5.00 kg |
122 °F @Load 11.0 lb |
|
LATI Latimass 53-04 D009 PP Homopolymer, Impact Modified Specific density compound based on Polypropylene homopolymer (PPh), impact modified. Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation.. |
|||
Vicat Softening Point | 50.0 °C @Load 5.00 kg |
122 °F @Load 11.0 lb |
|
LATI Latiohm 52/11-10 PD02 PP Homopolymer Dissipative product based on Polypropylene homopolymer (PPh). Unfilled.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria T.. |
|||
Vicat Softening Point | 50.0 - 129 °C | 122 - 264 °F | Average value: 115 °C Grade Count:14 |
Overview of materials for High Density Polyethylene (HDPE), Crosslinkable This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Crosslinkable". Each property range of values reported is minimum and .. |
|||
Vicat Softening Point | 50.0 °C @Load 5.00 kg |
122 °F @Load 11.0 lb |
|
LATI Latistat 48/9900-03 EVA Dissipative product based on Ethyl-Vinyl-Acetate (EVA). Unfilled. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termopl.. |