- Solvay Specialty Polymers Polidan® PNT 0856/35 Polyethylene, Crosslinked (XLPE)
Solvay Specialty Polymers Polidan® PNT 0856/35 Polyethylene, Crosslinked (XLPE)
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Crosslinkable |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Polidan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Polidan® PNT 0856/35 Polyethylene, Crosslinked (XLPE).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
POLIDAN® PNT 0856/35 is a silane crosslinkable PE compound which is used together with a catalyst masterbatch to accelerate the crosslinking reaction.Features: Crosslinkable; Good Flexibility; Low DensityUses: Connectors; Hose; Rubber ReplacementAdditional Properties: Extruder Screw Compression Ratio - >2.5:1; Extruder Screw L/D Ratio - 25:1 to 30:1; Gel Content - EN 579 > 65 %; Head Temperature - 200 °CInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.872 g/cc | 0.0315 lb/in³ | ASTM D792 |
| Melt Flow | 1.5 g/10 min | 1.5 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | >= 20.0 MPa | >= 2900 psi | ASTM D638 |
| Elongation at Break | >= 400 % | >= 400 % | ASTM D638 |
| Tensile Modulus | 0.00600 GPa | 0.870 ksi | ISO 527-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.450 - 0.470 W/m-K | 3.12 - 3.26 BTU-in/hr-ft²-°F | ASTM C177 |
| Vicat Softening Point | 50.0 °C | 122 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 150 - 200 °C | 302 - 392 °F | |
| Zone 2 | 150 - 200 °C | 302 - 392 °F | |
| Zone 3 | 150 - 200 °C | 302 - 392 °F | |
| Zone 4 | 150 - 200 °C | 302 - 392 °F | |
| Zone 5 | 150 - 200 °C | 302 - 392 °F | |
| Die Cooling Temperature | 210 °C | 410 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | DVGW W270; KTW Unspecified Rating | |
| Availability | Asia Pacific | |
| Europe | ||
| North America | ||
| Processing Technique | Extrusion; Pipe Extrusion |
Users viewing this material also viewed the following:
- MV Labs CU600 Cu2I2 Copper(I) iodide
- Network Polymers NPP 25-0105 TF20
- SABIC Innovative Plastics LNP LUBRICOMP CX05031 PS (Europe-Africa-Middle East)
- A. Schulman PP 3482-01 Polypropylene Nucleated Homopolymer Polypropylene
- Hexcel® HexPly® 954-2A Curing Cyanate Resin
- BASF Neopolen® P 9335 MG 0.04 g/cc Core density; Expanded Polypropylene (Europe)
- ArcelorMittal 13 High formability steel for drawing, Hot rolled
- DuPont Teijin Films Mylar® M30 Polyester Film, 100 Gauge (25 µm), PVDC Coated (discontinued **)
Copyright © lookpolymers.com All Rights Reserved