LATI Latimass 53-04 D009 PP Homopolymer, Impact Modified

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer	LATI
Trade Name	Latimass
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latimass 53-04 D009 PP Homopolymer, Impact Modified.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Specific density compound based on Polypropylene homopolymer (PPh), impact modified. Special filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	0.850 g/cc	0.0307 lb/in³
Linear Mold Shrinkage, Flow	0.013 - 0.016 cm/cm	0.013 - 0.016 in/in
Linear Mold Shrinkage, Transverse	0.0125 - 0.0155 cm/cm	0.0125 - 0.0155 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	8.00 MPa	1160 psi
Elongation at Break	55 %	55 %
Elongation at Yield	6.0 %	6.0 %
Tensile Modulus	0.900 GPa	131 ksi
Charpy Impact Unnotched	NB	NB
Charpy Impact, Notched	1.20 J/cm²	5.71 ft-lb/in²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	55.0 °C	131 °F
Deflection Temperature at 1.8 MPa (264 psi)	40.0 °C	104 °F
Vicat Softening Point	50.0 °C @Load 5.00 kg	122 °F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	220 - 240 °C	428 - 464 °F
Mold Temperature	40.0 - 60.0 °C	104 - 140 °F
Drying Temperature	80.0 - 90.0 °C @Time 10800 sec	176 - 194 °F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa