Techmer ES Luriblend® PA12 TS18
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 , Nylon 12, PTFE Filled |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PA12 TS18.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: Silicone Lubricant(2%) and PTFE Lubricant(18%)Features: LubricatedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Water Absorption | 0.50 % @Time 86400 sec |
0.50 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm @Thickness 3.17 mm |
0.015 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Yield | 58.6 MPa | 8500 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 68.9 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 1.65 GPa | 240 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm @Thickness 3.17 mm |
0.700 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 126 µm/m-°C | 70.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.8 °C | 172 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | ASTM D257 |
| Dielectric Strength | 25.6 kV/mm | 650 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Radici Radilon® A CP400 (dry) Nylon 66
- Total Lacqrene® 2551 Medium Impact Polystyrene (discontinued **)
- Karina E 805-48/1-IS-RG Black PVC Compound
- LyondellBasell Adsylâ„¢ 3 C 30 F HP Polypropylene Copolymer
- SABIC Innovative Plastics Ultem AUT230M PEI
- Eastman Tenite Butyrate 285A2R30010 Natural, Trsp Cellulose Acetate Butyrate
- Chevron Phillips MarFlex® 9659 HDPE Blown Film Resin
- Arlon 49581X010 0.0105" (0.267 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Ascend Performance Materials Vydyne® M344 BLK Nylon 66, Flame Retardant, DAM
Copyright © lookpolymers.com All Rights Reserved