Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 3.45 - 9.65 GPa | 500 - 1400 ksi | Average value: 6.85 GPa Grade Count:31 |
Overview of materials for Polyphthalamide (PPA), 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are.. |
|||
Flexural Modulus | 2.06 - 9.65 GPa | 299 - 1400 ksi | Average value: 2.75 GPa Grade Count:49 |
Overview of materials for Polyphenylene Ether, Heat Resistant This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, Heat Resistant". Each property range of values reported is minimum and maximum valu.. |
|||
Flexural Modulus | 3.33 - 9.65 GPa | 484 - 1400 ksi | Average value: 7.20 GPa Grade Count:89 |
Overview of materials for Polycarbonate, 30% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 30% Glass Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Flexural Modulus | 2.60 - 9.65 GPa | 377 - 1400 ksi | Average value: 3.97 GPa Grade Count:12 |
Overview of materials for Nylon 66, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Extruded". Each property range of values reported is minimum and maximum values of appropriate.. |
|||
Flexural Modulus | 1.80 - 9.65 GPa | 261 - 1400 ksi | Average value: 5.10 GPa Grade Count:34 |
Overview of materials for Nylon 66, 30% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Mineral Filled". Specific grades with primary filler content between 25% and 34% are inclu.. |
|||
Flexural Modulus | 8.27 - 9.65 GPa | 1200 - 1400 ksi | |
Bulk Molding Compounds BMC T14 General Purpose Molding Compound BMC T14 is a general purpose molding compound. Due to the excellent flow and controlled reactivity, BMC T14 is well suited for injection, transfer or compression molding of intricate parts. Typica.. |
|||
Flexural Modulus | 8.27 - 9.65 GPa | 1200 - 1400 ksi | |
Bulk Molding Compounds BMC T9 General Purpose Molding Compound BMC T9 is a low cost, general purpose bulk molding compound designed for the electrical industry. It is UL listed and is used extensively in the manufacture of residential circuit breakers. BMC T9.. |
|||
Flexural Modulus | 8.27 - 9.65 GPa | 1200 - 1400 ksi | |
Bulk Molding Compounds BMC A50-MS General Purpose Molding Compound BMC A50-MS is a medium strength, high appearance, general purpose molding compound. Due to the excellent flow and controlled reactivity, BMC A50-MS is well suited for injection, transfer or compres.. |
|||
Flexural Modulus | 2.96 - 9.65 GPa | 430 - 1400 ksi | Average value: 7.58 GPa Grade Count:11 |
Overview of materials for Nylon 46, Lubricated + Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Lubricated + Glass Fiber Reinforced". Each property range of values reported is minimum and ma.. |
|||
Flexural Modulus | 1.90 - 9.65 GPa | 276 - 1400 ksi | Average value: 4.72 GPa Grade Count:26 |
Overview of materials for Polybutylene Terephthalate (PBT), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Mineral Filled". Each property range of values reported is minimum and.. |
|||
Flexural Modulus | 2.25 - 9.66 GPa @Temperature -40.0 - 150 °C |
326 - 1400 ksi @Temperature -40.0 - 302 °F |
Average value: 4.77 GPa Grade Count:3 |
Overview of materials for Polyethylene Terephthalate (PET), 30% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 30% Glass Reinforced". Specific grades with glass content between 25% .. |
|||
Flexural Modulus | 8.27 - 9.65 GPa | 1200 - 1400 ksi | ASTM D790 |
Premix Premi-Glas® 1200H-24 Polyester SMC
(discontinued **) Premi-Glas® 1200H-24 is a 24% fiberglass reinforced, thermoset, Sheet Molding Compound designed for applications where arc resistance and dielectric strength are required and UL 94 HB flame recogni.. |
|||
Flexural Modulus | 8.27 - 9.65 GPa | 1200 - 1400 ksi | ASTM D790 |
Premix Premi-Glas® 1200-24 Polyester SMC
(discontinued **) Premi-Glas® 1200-24 is a 24% fiberglass-reinforced, thermoset, sheet molding compound designed for Class A Heavy Truck - Bus body panels and Marine cowls parts where smooth, flat, ripple free surfa.. |
|||
Flexural Modulus | 8.27 - 9.65 GPa | 1200 - 1400 ksi | ASTM D790 |
Premix Premi-Glas® 1200-28 Polyester SMC
(discontinued **) Premi-Glas® 1200-28 series is a low profile, 28 % glass reinforced polyester Sheet Molding Compound designed for recreational vehicle body panels applications that require excellent flexibility and.. |