Polymer Property : Flexural Modulus = 943 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	6.50 GPa	943 ksi	STN EN ISO 178
Plastcom PLASTAMID® 6 GF 30 002 TS PA6 reinforced with glass fiber, heat stabilized PA 6 for injection molding, reinforced with 30% glass fiber, heat stabilized. Decrease in tensile strength by 50 % after 5000 hours at 170°C. Used for holders of hand tools, hobby tools, gear wheel..
Flexural Modulus	6.50 GPa	943 ksi	ISO 178
Nilit FRIANYL A63 FK 2010 Nylon 6.6 for injection molding, 20% glass fiber and 10% glass ball reinforced Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Modulus	6.50 - 12.1348 GPa @Temperature -40.0 - 120 °C	943 - 1760.03 ksi @Temperature -40.0 - 248 °F	Average value: 9.41 GPa Grade Count:2
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler". Specific grades with glass content between 25%..
Flexural Modulus	6.50 GPa	943 ksi
Lehmann & Voss LUVOCOMÂ® 1105-8451 PEEK, with carbon fiber, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precisio..
Flexural Modulus	6.50 GPa	943 ksi
Lehmann & Voss LUVOCOMÂ® 50/CF/10/TF/15/BK 100 Polycarbonate, with carbon fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi..
Flexural Modulus	6.50 GPa	943 ksi
Lehmann & Voss LUVOCOMÂ® 1/GF/20/TF/10/SI/2/NC Polyamide 66, with glass fiber, PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Strong, stiff parts.Bearings, ..
Flexural Modulus	6.50 GPa	943 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem 2200N PEI (Asia Pacific) 20% Glass fiber filled Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Modulus	6.50 GPa	943 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM 2210F PEI 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors.
Flexural Modulus	6.50 GPa	943 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM HU2210 PEI 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP ..
Flexural Modulus	6.50 GPa	943 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics Ultem PW2200 PEI (Europe-Africa-Middle East) 20% Glass fiber filled, standard flow Polyetherimide (Tg 217Â°C). Product designed and certified for use in Potable Water applications. KTW, WRAS, ACS certified. NSF61 and W270 pending. US FDA and..
Flexural Modulus	6.50 GPa	943 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Stat-kon DE002E PC (Europe-Africa-Middle East) LNP* STATKON* DE002E is a compound based on Polycarbonate resin containing Carbon Fiber. Added features include; Easy Molding.This data was supplied by SABIC-IP for the Europe-Africa-Middle East reg..
Flexural Modulus	6.50 GPa	943 ksi	3-Point Bending; ISO 178
Styron INSPIREâ„¢ DLGF 9621.00 Compounded Polypropylene, 60% LGF Overview: DLGF 9621.00 is a polypropylene homopolymer reinforced with 60% by weight of long glass fiber. PP-LGF60, Long Glassfiber Granulate). DLGF 9621.00 is produced by pultrusion/melt-impregnatio..
Flexural Modulus	6.50 GPa	943 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP WF0049 PBT (Europe-Africa-Middle East) LNP* Thermocomp* WF0049 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant.
Flexural Modulus	6.50 GPa	943 ksi	ASTM D790
Plenco 7203 Phenolic, Granular, Transfer Molded PLENCO 07203 is an organic fiber reinforced phenolic molding compound, offering improved mechanical strength and an industrial finish. UL recognized under component file E40654. 07203 is available i..
Flexural Modulus	>= 6.50 GPa	>= 943 ksi	ASTM-D790
Polyram PlusTek RB300G6 Nylon 6, 30% Glass Fiber 30% glass-fiber reinforced polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Modulus	6.50 GPa	943 ksi	ASTM-D790
Polyram RamSter PF320G4 PBT, 20% Glass Fiber, Flame Retardant 20% Glass fiber reinforced, flame retardant PBT for injection molding applicationsInformation provided by Polyram Ram On Ind.
Flexural Modulus	6.50 GPa	943 ksi	ISO 178
Polyram PlusTek PB300G4 Nylon 6 for Injection Molding, 20% Glass-Fiber Reinforced 20% Glass fiber reinforced, heat stabilized Nylon 6 for injection molding applications.Information provided by Polyram.
Flexural Modulus	6.50 GPa	943 ksi	ASTM D 790
Cossa Polimeri ESTADIENE 0460 GF Acrylonitrile Butadiene Styrene, 30% Glass Filled ABS with 30% glass fiber reinforcementExcellent dimensional stability, low shrinkage, good impact resistanceInformation provided by Cossa Polimeri S.r.l.
Flexural Modulus	6.50 GPa	943 ksi	DAM; ISO 178
DuPont Performance Polymers Zytel® PLS FR95G15DH2 BK269 Nylon 6 15% Glass Reinforced Flame Retardant Heat Stabilized Polyamide Zytel PLSFR95G15DH2 BK269 is 15% glass reinforced flame retardant black PA using SHIELD Technology only from DuPont exceptional resista..
Flexural Modulus	6.50 GPa	943 ksi	ISO 178
Eurotec® Tecodur® PB70 GR20 NL CA 01 PBT/PET 20% glass fiber reinforced Excellent stiffness and hardnessGood mechanical strengthGood creep and fatigue behaviorVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance..
Flexural Modulus	6.50 GPa	943 ksi	ISO 178
Ascend Performance Materials Vydyne® R533 NT Nylon 66, 33% Glass Reinforced, Conditioned Vydyne® R533 NT is general-purpose, 33% glass-fiber reinforced PA66 resin. Available in natural, it is an injection-molding grade that is lubricated for good machine feed, flow and mold release. Gl..
Flexural Modulus	6.50 GPa	943 ksi	ASTM D790
Ascend Performance Materials VYDYNE® R533H Nylon, 33% Glass Reinforced, Conditioned Vydyne® R533H is 33% glass-fiber reinforced, heat-stabilized PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties when exposed to anti-free..
Flexural Modulus	6.50 GPa	943 ksi	ISO 178
BASF Ultramid® A3EG6 30% Glass Filled PA66 (Conditioned) Ultramid A3EG6 is a 30% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability.
Flexural Modulus	6.50 GPa	943 ksi	ASTM D790
Beijing Ranger Chem PBT-201-G10 Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin..
Flexural Modulus	6.50 GPa	943 ksi	ISO 178
Ascend Performance Materials Vydyne® R533H BK02 Nylon 66, 33% Glass Reinforced, Conditioned Vydyne® R533H BK02 is 33% glass-fiber reinforced, heat-stabilized PA66 resin. Available in black, it is specifically designed to maximize the retention of physical properties when exposed to anti-f..
Flexural Modulus	6.50 GPa	943 ksi	ISO 178
Ascend Performance Materials Vydyne® R533H NT Nylon 66, 33% Glass Reinforced, Conditioned Vydyne® R533H NT is 33% glass-fiber reinforced, hydrolysis-resistant, heat-stabilized PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties ..
Flexural Modulus	6.50 GPa	943 ksi	ISO 178
Gharda Chemicals GAFONE™ 3420GF PES, Glass Fiber-Reinforced (discontinued **) Glass fiber reinforced granules for injection molding. With lower viscosity for molding intricate cross sections.Characteristics: Very high rigidityGood dielectric propertiesHigh mechanical strengt..