SABIC Innovative Plastics LNP Stat-kon DE002E PC (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP STAT-KON
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP Stat-kon DE002E PC (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* STATKON* DE002E is a compound based on Polycarbonate resin containing Carbon Fiber. Added features include; Easy Molding.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.

Physical Properties	Metric	English	Comments
Density	1.23 g/cc	0.0444 lb/inÂ³	ISO 1183
Water Absorption	0.21 % @Temperature 23.0 Â°C, Time 86400 sec	0.21 % @Temperature 73.4 Â°F, Time 24.0 hour	ISO 62-1
Linear Mold Shrinkage, Flow	0.0017 cm/cm	0.0017 in/in	SABIC Method

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	117 MPa	17000 psi	5 mm/min; ISO 527
Elongation at Break	1.8 %	1.8 %	5 mm/min; ISO 527
	2.9 %	2.9 %	Flexural Strain, 2 mm/min; ISO 178
Tensile Modulus	8.60 GPa	1250 ksi	1 mm/min; ISO 527
Flexural Strength	150 MPa	21800 psi	2 mm/min; ISO 178
Flexural Yield Strength	157 MPa	22800 psi	2 mm/min; ISO 178
Flexural Modulus	6.50 GPa	943 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	7.00 kJ/mÂ² @Temperature 23.0 Â°C	3.33 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	30.0 kJ/mÂ² @Temperature 23.0 Â°C	14.3 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1U

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	139 Â°C	282 Â°F	Flatw 80104 sp=64mm; ISO 75/Af