Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 5.00 GPa | 725 ksi | 1.3 mm/min; ASTM D790 |
Ovation Polymers Opnyl OP6GF15 Nylon 6, 15% Glass Reinforced, Dry Nylon 6 - Glass reinforced (15 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. For Nylon compounds the m.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D790 |
Polymer Resources PC-G20-[color]-WS Polycarbonate, 20% Glass Reinforced Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Flexural Modulus | 5.00 - 7.00 GPa | 725 - 1020 ksi | Compression; ISO 178 |
Raschig Group AMPLA® 2500 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Excellent elasticity and shock resistance, low post-shrinkage, very good electrical values, high heat.. |
|||
Flexural Modulus | 5.00 GPa @Temperature 23.0 °C |
725 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PPC GF15030 PD2 Polypropylene Copolymer, Glass Fiber Reinforced, Chemically Coupled Information provided by Polykemi AB |
|||
Flexural Modulus | 5.00 GPa @Temperature 90.0 °C |
725 ksi @Temperature 194 °F |
ISO 178, ASTM D790 |
Nilit Nilamid B3 H G6 30% Glass Fiber Reinforced PA6 Description: Nilamid B3 H G6 is a general purpose, 30% glass fiber reinforced NYLON 6 with a combination of good mechanical performance, impact strength and processability. It is one of the most wid.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 3412ECR PC (Europe-Africa-Middle East) Lexan* 3412ECR Polycarbonate (PC) resin is a 20% glass fiber filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant GF-PC has an UL-94 V0 rating and is available in v.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
Nilit FRIANYL B63 SG-GV 2010 Nylon 6 for injection molding, 20% mineral filled and 10% glass fiber reinforced Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | |
Lehmann & Voss LUVOCOM® 1105-7809/BK PEEK, with glass fiber, easy flowing Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts.Chemical and hydrolysis resistance parts, non flammable.High dimension.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D790 |
Loxim 330 12V0 Nylon 6 Information provided by Loxim Industries |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | |
Lehmann & Voss LUVOCOM® 1105-7310 PEEK, with glass fiber, easy flowing, low-warpage Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.High dimensionally stable precision parts, high continuous use temperature.Superheated ste.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | |
Lehmann & Voss LUVOCOM® 1100/GF/20/EM/MR/BK Polyether sulfone, with glass fiber, easy flowing, demolding aid Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.High dimensionally sta.. |
|||
Flexural Modulus | 5.00 GPa @Temperature 150 °C |
725 ksi @Temperature 302 °F |
ISO 178 |
Solvay Specialty Polymers Amodel® AFA-6133 V0 Z Polyphthalamide (PPA), 33% Glass Fiber (Conditioned) Amodel® AFA-6133 V0 Z is a 33% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both in.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® VX8015U PBT+PET (Europe-Africa-Middle East) VALOX VX8015U is a UV stabilized, 15% glass reinforced PBT+PET injection moulding resin with improved surface finish quality characteristics versus VALOX 815. This grade is 815 with improved gloss a.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
Solvay TECHNYL® A 218 MT15 V 25 Black 21N PA66, 25/15% glass/mineral fiber, Conditioned Description: Polyamide 66, reinforced with 25% of glass fiber and 15% of mineral filler, heat stabilized, for injection molding.Available in: Asia PacificProduct Applications: TECHNYL® A 218 MT15.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
Polyram PlusTek PA320G3 Nylon 6.6 for Injection Molding, 15% Glass Fiber Reinforced, Flame Retardant 15% Glass fiber reinforced flame retardant Nylon 6.6 for injection molding applications.Information provided by Polyram. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | D790 |
Zhejiang Juner 301-G15 15% Glass Fibre Reinforced and Flammable Resistant Applications: Electrons and Electricity: TV Components, Plugs of Computers, Exhaust Fans of Computers, Plugs, Sockets, Shells of Electronics, Framework of Level Output Transformers, Pipe Pedestals, .. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 |
Polyram PlusTek PB305G33BK37 Nylon 6, 33% Glass Fiber Reinforced, UV and Heat Stabilized 33% Glass fiber reinforced, UV and heat stabilized Nylon 6. Approved and listed by W.R.A.S. and NSF/ANSI 61 International for potable water.Information provided by Polyram. |
|||
Flexural Modulus | >= 5.00 GPa | >= 725 ksi | ASTM-D790 |
Polyram PlusTek RA300G4 Nylon 6.6, 20% Glass Fiber 20% glass fiber reinforced polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | DAM; ISO 178 |
DuPont Performance Polymers Zytel® 73G15L NC010 Nylon 6
(Unverified Data**) 15% Glass Reinforced Polyamide 6Zytel 73G15L NC010 is a 15% glass fiber reinforced polyamide 6 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
Flexural Modulus | >= 5.00 GPa | >= 725 ksi | IEC 1212-2 5.2 |
Hippe MF CC 201 Woven Cotton Cloth Reinforced Melamine Resin - Sheet Used in mechanical and electrical applications (coarse weave: >130 g/m2, =30 threads/cm). Arc and tracking resistant.Information provided by Hippe. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | from bending test; DIN 53 457 |
Hippe PAI Polyamide-imide Particularly used where high strength in a wide range of temperature (-190°C…+260°C), high notched strength and very good dielectric properties are required. Features good chemical stability, fl.. |
|||
Flexural Modulus | >= 5.00 GPa | >= 725 ksi | IEC 1212-2 5.2 |
Hippe PF CP 207 Cellulose Paper Reinforced Phenolic Resin - Sheet Used in mechanical applications. Used in mechanical properties better than other PF CP types. Poor electrical properties under normal humidity. Also available in hot-punching versions. Improved .. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D790 |
Adell BR-13 Nylon 6, 15% Glass Reinforced Data provided by Adell Plastics, Inc. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ASTM D790 |
Beijing Chemical Industry KAIFA® 551-GT30S PBT Resin Glass fiber and mineral filled, flame retardant, low warpage, superior electrical performanceInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Flexural Modulus | 5.00 - 8.00 GPa | 725 - 1160 ksi | ISO 178 |
Bulk Molding Compounds tetra-DUR F 4001 Bulk Molding Compound UL-Licensed, Abrasion resistance, free of fiber glass.Typical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipati.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | 2 [mm/min]; ISO 178 |
Akro-Plastic Akromid® A3 GF 20 (2419) PA 6.6 Conditioned, 20% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | ISO data |
BASF Capron® 8260 HS BK-102 40% Mineral-Filled Nylon 6 (Dry)
(discontinued **) Capron 8260 HS BK-102 is a heat stabilized, pigmented black, 40% mineral reinforced nylon 6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined .. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Lexan® 3412ECR PC (Asia Pacific) Lexan* 3412ECR Polycarbonate (PC) resin is a 20% glass fiber filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant GF-PC has an UL-94 V0 rating and is available in v.. |
|||
Flexural Modulus | 5.00 GPa | 725 ksi | |
Lehmann & Voss LUVOCOM® 1301-8291 PPS, linear, with aramid reinforcement Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.Improved friction and wear behaviour. Emergency running property.Low warpage.dynamic stressInforma.. |