- Lehmann & Voss LUVOCOM® 1100/GF/20/EM/MR/BK Polyether sulfone, with glass fiber, easy flowing, demolding aid
Lehmann & Voss LUVOCOM® 1100/GF/20/EM/MR/BK Polyether sulfone, with glass fiber, easy flowing, demolding aid
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 10%Glass Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1100/GF/20/EM/MR/BK Polyether sulfone, with glass fiber, easy flowing, demolding aid.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Apparatus- and precision engineering, film- and photo industry, sporting- and leisure goods, medical- and electrical enineering, aircraft- and aerospace industry.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance range.Especially suitable for thin wall complex parts.Especially suitable for medical parts, superheated steam sterilizable, hydrolysis resistanceHigh quality terminal bar, switches and plugs, relais, lamp reflectors, sterilizable medical equipment.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 300 °C |
15 g/10 min @Load 4.76 lb, Temperature 572 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 115 MPa | 16700 psi | |
| Elongation at Yield | 2.2 % | 2.2 % | |
| 3.5 % | 3.5 % | flexural | |
| Modulus of Elasticity | 6.00 GPa | 870 ksi | |
| Flexural Strength | 160 MPa | 23200 psi | |
| Flexural Modulus | 5.00 GPa | 725 ksi | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | flatwise; ISO 179 1fU |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 31.0 µm/m-°C | 17.2 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 180 °C | 356 °F | |
| 200 °C | 392 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | |
| Vicat Softening Point | 220 °C | 428 °F | DIN ISO 306 |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 350 °C | 662 °F | mass temp |
| Nozzle Temperature | 340 - 360 °C | 644 - 680 °F | |
| Zone 1 | 355 - 375 °C | 671 - 707 °F | |
| Zone 2 | 360 - 380 °C | 680 - 716 °F | |
| Zone 3 | 350 - 370 °C | 662 - 698 °F | |
| Mold Temperature | 120 - 200 °C | 248 - 392 °F | |
| Drying Temperature | 150 °C @Time 10800 - 18000 sec |
302 °F @Time 3.00 - 5.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- Nyco M3 WOLLASTOCOAT® Wollastonite
- Nylene® NX4528 Unfilled Nylon 6,6/6
- SABIC PP 674K Polypropylene Copolymer for Injection Molding
- Abatron AboCast 8101-3/AboCure 8101-3 Epoxy (discontinued **)
- Silberline Sparkle Silver® Premier 354
- Polyplastics TOPAS® 6015 Cyclic Olefin Copolymer (COC) (Asia/Pacific Grade)
- A. Schulman POLYBATCH™ Beige 6027E Concentrate Based In Polyethylene
- BASF Ultramid® 8267G HS BK-106A 15/25% Glass/Mineral Filled PA6 (Conditioned)
- SABIC Innovative Plastics LNP KONDUIT PX11313 PA 6 (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved