Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 7.93 GPa | 1150 ksi | ASTM D790 |
Polymer Resources TP-GFMF2 Polybutylene Terephthalate, 40% Glass/Mineral Reinforced Polybutylene Terephthalate, 40% Glass/Mineral ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informat.. |
|||
Flexural Modulus | 7.90 GPa | 1150 ksi | ISO 178 |
Nilit FRIANYL B63 HS-GV40 Nylon 6 for injection molding, 40% glass fiber reinforced Nylon 6 for injection molding, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 7.92 GPa | 1150 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP DFL16E PC (Asia Pacific) LNP* Lubricomp* DFL16E is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Easy Molding. |
|||
Flexural Modulus | 7.90 GPa | 1150 ksi | ISO 178 |
Solvay TECHNYL® A 218G1 V25 Black 34N PA66, 25% glass fiber, DRY Description: Polyamide 66, reinforced with 25% of glass fiber, for injection molding. This grade shows an improved retention of properties after long term ageing in automotive cooling liquids. Avail.. |
|||
Flexural Modulus | 7.92 GPa | 1150 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP IFL36 PA6.12 LNP LUBRICOMP* IFL36 is a compound based on Nylon 6/12 resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant. |
|||
Flexural Modulus | 7.90 GPa | 1150 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® 771 PBT (Europe-Africa-Middle East) VALOX 771 is a 15% glass and 20% mineral filled, flame retarded injection moulding PBT resin. |
|||
Flexural Modulus | 7.94 GPa | 1150 ksi | ASTM D790 |
SABIC Innovative Plastics NORYL HM3020H PPE+PS (Asia Pacific) PPE+PS GF+MF 30% filled, FR V-1, high flow |
|||
Flexural Modulus | 7.92 GPa | 1150 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP XFL36 AMORPHOUS POLYAMIDE LNP* LUBRICOMP* XFL36 is a compound based on Amorphous Nylon containing 30% Glass Fiber and 15% PTFE. Added feature of this material is: Wear Resistant. |
|||
Flexural Modulus | 7.93 GPa | 1150 ksi | ASTM D790 |
Teknor Apex Chemlon® 125-15 MGH Nylon 66, 25% Mineral Reinforced, 15% Glass Fiber Reinforced Notes: 25% Mineral - 15% Glass; Excellent stiffness and strength, especially at high temperatures, with improved warpage control over glass reinforced products; FMVSS Flammability: Passes, FMVSS 302.. |
|||
Flexural Modulus | 7.95 GPa | 1150 ksi | Tangent; ISO 178 |
A. Schulman FORMION™ FI 226 40% Glass Fiber Reinforced Ionomer / Nylon Alloy DescriptionFormion® FI 226 is an injection molding grade, 40% glass fiber reinforced Ionomer / Nylon alloy, which has been formulated for high scratch resistance, heat resistance and high stiffness.. |
|||
Flexural Modulus | 7.90 GPa | 1150 ksi | ISO 178-93 |
Wellman Wellamid® GFT1675-N1 33% Glass Fiber Reinforced, Impact Modified Nylon 66 Description: Glass Fiber Reinforced, Impact Modified Nylon 66Information provided by Wellman. |
|||
Flexural Modulus | 7.93 GPa | 1150 ksi | Tangent; ASTM D790 |
Plastics Group Polifil® GFPC-30 30% Glass-Reinforced Polycarbonate Polifil® GFPC series compounds offer a combination of improved dimensional stability and decreased flammability. The excellent balance of physical properties make the Polifil® glass-filled polycar.. |
|||
Flexural Modulus | 7.93 GPa | 1150 ksi | ASTM D790 |
A. Schulman LUBRILON® 432 30% Glass Fiber Reinforced, PTFE Lubricated PBT Alloy Information provided by A. Schulman. |
|||
Flexural Modulus | 7.90 GPa | 1150 ksi | ISO 178 |
BASF Ultramid® 66 H2 G/25-V0KB1 NAT 0046 PA66 (Dry) Information provided by BASF |
|||
Flexural Modulus | 7.90 GPa | 1150 ksi | ISO 178 |
BASF Ultramid® S3WG6 Balance 30% Glass Filled PA 610 (Dry) Description: BASF supplies polyamide 610 for processing by injection molding under the trade name Ultramid® Balance which is produced by polycondensation of hexamethylene diamine and sebacic acid. .. |
|||
Flexural Modulus | 7.90 GPa | 1150 ksi | ASTM D790 |
Ashley Polymers Ashlene® 520-33G Nylon 66, 33% Glass Reinforced Nylon 66, 33% glass reinforced resin. Also available with Heat Stabilized and/or UV Stabilized.Data provided by the manufacturer |
|||
Flexural Modulus | 7.90 GPa | 1150 ksi | ISO 178 |
Polyplastic Armamid® PA6 GF 30-2HSM-902 Nylon, 30% Glass Filled Heat stabilizedInformation provided by PolyPlastic Group. |
|||
Flexural Modulus | 7.90 GPa | 1150 ksi | ISO 178 |
Polyplastics Duracon® GH-25D Acetal Co-polymer (POM), GF 25% reinforced, High flow, High strength, High rigidity DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |
|||
Flexural Modulus | 7.90 GPa | 1150 ksi | ISO 178 |
Polyplastics Duracon® GH-25 Acetal Co-polymer (POM), GF 25% reinforced, High strength, High rigidity DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |