- Teknor Apex Chemlon® 125-15 MGH Nylon 66, 25% Mineral Reinforced, 15% Glass Fiber Reinforced
Teknor Apex Chemlon® 125-15 MGH Nylon 66, 25% Mineral Reinforced, 15% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled , Nylon 66, 30% Mineral Filled |
| Manufacturer | Teknor Apex Company |
| Trade Name | Chemlon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Chemlon® 125-15 MGH Nylon 66, 25% Mineral Reinforced, 15% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Notes: 25% Mineral - 15% Glass; Excellent stiffness and strength, especially at high temperatures, with improved warpage control over glass reinforced products; FMVSS Flammability: Passes, FMVSS 302 Features: Heat Stabilized Processing Method: Injection Method Forms: Pellets Automotive Specifications: Chrysler Ms-DB41 CPN2554 Color: BK001 BlackInformation Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0015 - 0.0040 cm/cm | 0.0015 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 128 MPa | 18500 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Elongation at Yield | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 190 MPa | 27500 psi | ASTM D790 |
| Flexural Modulus | 7.93 GPa | 1150 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm @Temperature 22.8 °C |
1.40 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | DSC |
| Deflection Temperature at 1.8 MPa (264 psi) | 241 °C | 465 °F | Unannealed; ASTM D648 |
| UL RTI, Electrical | 65.0 °C @Thickness 0.749 mm |
149 °F @Thickness 0.0295 in |
UL 746 |
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.749 mm |
149 °F @Thickness 0.0295 in |
UL 746 |
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.749 mm |
149 °F @Thickness 0.0295 in |
UL 746 |
| Flammability, UL94 | HB @Thickness 0.749 mm |
HB @Thickness 0.0295 in |
|
| Oxygen Index | 24 % | 24 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 550 V | 550 V | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 241 - 257 °C | 465 - 495 °F | |
| Middle Barrel Temperature | 263 - 279 °C | 505 - 535 °F | |
| Front Barrel Temperature | 268 - 285 °C | 515 - 545 °F | |
| Nozzle Temperature | 268 - 282 °C | 515 - 540 °F | |
| Melt Temperature | 263 - 285 °C | 505 - 545 °F | Processing Temperature |
| Drying Temperature | 79.4 °C | 175 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Suggested Moisture, max | 0.2 | |
| Suggested Regrind, max | 25 |
Users viewing this material also viewed the following:
- Nylene® PA6/6 Glass Filled 5143 HS Nylon 6/6
- Gouda Vuurvast CURAS 90 Moldable Refractory Material
- Zeon Chemicals HyTemp® 4051 AR Polyacrylate Elastomer
- Eastman Drystar 0325 Copolyester
- DuPont Performance Polymers Kalrez® AeroSeal™ 7797 Fluoroelastomer
- C.O.I.M. FILCO® 657 Unsaturated Polyester Powder Resin
- BASF N-Methylacetamide
- Ashley Polymers Ashlene® 630-13G Nylon 6, 13% Glass Reinforced
- Lubriplate MAG-00 Lithium-Polymer Type Grease For Special Applications / Conditions
Copyright © lookpolymers.com All Rights Reserved