Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 7.70 GPa @Temperature 23.0 °C |
1120 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYshine PBT D221 GF30 PBT, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
Flexural Modulus | 7.70 GPa @Temperature 23.0 °C |
1120 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB SCANMID 6 B12^ F25 Nylon 6, Glass Fiber Reinforced Information provided by Polykemi AB |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
Nilit FRIANYL A63 HH-GV30 Nylon 6.6 for injection molding, 30% glass fiber reinforced Nylon 6.6 for injection molding, heat and hydrolysis stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
Nilit FRIANYL B63 HS-GV35 Nylon 6 for injection molding, 35% glass fiber reinforced Nylon 6 for injection molding, high impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | 2 [mm/min]; ISO 178 |
Akro-Plastic Akromid® S3 GF 30 4 (3552) PA 6.10 Dry, 30% Glass Filled
(discontinued **) A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw materia.. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP JFL36 PES (Europe-Africa-Middle East) LNP* Lubricomp* JFL36 is a compound based on Polyethersulfone resin containing Glass Fiber, PTFE. |
|||
Flexural Modulus | 7.72 GPa | 1120 ksi | ISO 178 |
Solvay Specialty Polymers KetaSpire® KT-880 GF20 Polyetheretherketone (PEEK), 20% Glass Fiber KetaSpire® KT-880 GF20 is a high flow, 20% glass-fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpi.. |
|||
Flexural Modulus | 7.72 GPa | 1120 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® SHF436HR PBT (Asia Pacific) PBT, Super High Flow, 30% glass reinforced,hydrolytically resistant. |
|||
Flexural Modulus | 7.72 GPa | 1120 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP LF004E PEEK LNP* THERMOCOMP* LF004E is a compound based on Polyetheretherketone resin containing 20% Glass Fiber. Added features of this material include: Easy Molding. |
|||
Flexural Modulus | 7.75 GPa | 1120 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® GR-4030 ABS, 30% Glass Filled Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 7.75 GPa | 1120 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Starex® GR-4030 ABS, 30% Glass Filled Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP VERTON MV007SU PP (Europe-Africa-Middle East) LNP* VERTON * MV007SU is a compound based on PP resin containing Long Glass Fiber. Added features include; Chemically Coupled, Heat Stabilized, UV Stabilizedl. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP VERTON MV007SUP PP (Europe-Africa-Middle East) LNP* VERTON* MV007SUP is a compound based on PP resin containing Long Glass Fiber. Added features include; Chemically Coupled, Heat Stabilized, UV Stabilized. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP VERTON MV007U PP (Europe-Africa-Middle East) LNP* VERTON* MV007U is a compound based on PP resin containing Long Glass Fiber. Added features include; Chemically Coupled, Heat Stabilized, UV Stabilized. |
|||
Flexural Modulus | 7.72 GPa | 1120 ksi | ASTM D790 |
Techmer ES HiFill® ABS GF30 HT 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightInformation provided by TP Composites, Inc. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
SABIC Innovative Plastics LNP Thermocomp RFB53SUZ PA 66 LNP THERMOCOMP* RFB53SUZ is a compound based on Nylon 66 resin containing Glass Bead, Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for th.. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ASTM D790 |
Plenco 00732 Melamine-Phenolic, Granular, Injection Molded PLENCO 00732 is a melamine-phenolic copolymer molding compound, exhibiting excellent electrical and flame resistant properties. Type ASTM 5948 CMG, and UL recognized under component file E40654. 007.. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ASTM D790 |
Plenco 3557 Phenolic, Granular, Compression Molded PLENCO 03557 is a woodflour and mineral filled phenolic molding compound offering excellent dielectric strength values at elevated temperatures while maintaining mechanical strength properties. UL r.. |
|||
Flexural Modulus | 7.72 GPa | 1120 ksi | dry; ISO 178 |
DSM Akulon® Ultraflow K-FHGM35 PA6-(GF+MD)40 15% Glass Reinforced, Heat Stabilized, High Flow |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
DuPont Performance Polymers Crastin® HR5330HF NC010 Polybutylene Terephthalate (PBT)
(Unverified Data**)& 30% Glass Reinforced Hydrolysis Resistant Polybutylene Terephthalate Crastin HR5330HF is a 30% glass reinforced PBT with high flow (HF) moderately toughened hydrolysis resistant (HR) resin. Excellen.. |
|||
Flexural Modulus | 7.75 GPa | 1120 ksi | ISO 178 |
Eurotec® Tecomid® NA40 GR25 NL PA 6.6 25% glass fiber reinforced Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good.. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
Ascend Performance Materials Vydyne® R525H BLK Nylon 66, 25% Glass Reinforced, DAM Vydyne® R525H BLK is hydrolysis-resistant, 25% glass-fiber reinforced, heat-stabilized PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties.. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ASTM D790 |
LATI LARPEEK 50 G/20 20% Glass Reinforced Polyetheretherketone (PEEK)
(discontinued **) Larpeek polyetheretherketone (PEEK) is a high performance thermoplastic offering cost effective performance in difficult environments across all industries. PEEK is temperature resistant (up to 250°.. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Verton PV007SV_YW8D151 PA 6 Preliminary data for 35% long fiber single pellet color filled PA6This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® VX4930 PBT (Europe-Africa-Middle East) VALOX VX4930 is a 30% glass reinforced nucleated PBT/ASA blend with excellent mechanical properties, high dimensional stability and low density. Applications: connectors and automotive industry. |
|||
Flexural Modulus | 7.72 GPa | 1120 ksi | ASTM D790 |
Plenco 6554 Phenolic, Granular, Compression Molded
(discontinued **) Two-Stage Phenolic. PLENCO 06554 is an organic reinforced phenolic molding compound modified with PTFE to offer improved coefficient of friction values. 06554 is available in black.Information supp.. |
|||
Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
Ascend Performance Materials Vydyne® R525H Nat Nylon 66, 25% Glass Reinforced, DAM Vydyne® R525H Nat is hydrolysis-resistant, 25% glass-fiber reinforced, heat-stabilized PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties.. |
|||
Flexural Modulus | 7.72 GPa @Temperature 100 °C |
1120 ksi @Temperature 212 °F |
ISO 178 |
Solvay Specialty Polymers Amodel® A-4133 L Polyphthalamide (PPA), Dry
(discontinued **) Amodel A-4133L polyphthalamide (PPA) is a 33% glass reinforced resin designed to offer high crystallinity when molded in water-cooled molds. Key properties include high heat resistance, reduced outg.. |