DuPont Performance Polymers Crastin® HR5330HF NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)&

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF DuPont Performance Polymers Crastin® HR5330HF NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)&.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
30% Glass Reinforced Hydrolysis Resistant Polybutylene Terephthalate Crastin HR5330HF is a 30% glass reinforced PBT with high flow (HF) moderately toughened hydrolysis resistant (HR) resin. Excellent balance of properties between terminal pullout and iInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.29 g/cc
0.0466 lb/in³
1.50 g/cc
0.0542 lb/in³
ISO 1183
Water Absorption 0.35 %
<br>@Thickness 2.00 mm
 0.35 %
<br>@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.150 %
<br>@Thickness 2.00 mm
 0.150 %
<br>@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 68560 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 260 °C
 68560 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 500 °F
 ISO 11403-1 -2
79300 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 250 °C
 79300 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 482 °F
 ISO 11403-1 -2
92760 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 240 °C
 92760 cP
<br>@Shear Rate 5000 1/s,<br> Temperature 464 °F
 ISO 11403-1 -2
221300 cP
<br>@Shear Rate 500 1/s,<br> Temperature 260 °C
 221300 cP
<br>@Shear Rate 500 1/s,<br> Temperature 500 °F
 ISO 11403-1 -2
260930 cP
<br>@Shear Rate 500 1/s,<br> Temperature 250 °C
 260930 cP
<br>@Shear Rate 500 1/s,<br> Temperature 482 °F
 ISO 11403-1 -2
310000 cP
<br>@Shear Rate 500 1/s,<br> Temperature 240 °C
 310000 cP
<br>@Shear Rate 500 1/s,<br> Temperature 464 °F
 ISO 11403-1 -2
Viscosity Test 95 cm³/g
95 cm³/g
ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 132 MPa
19100 psi
ISO 527-1/-2
Tensile Stress 11.63 MPa
<br>@Strain 0.370 %,<br> Temperature 150 °C
 1687 psi
<br>@Strain 0.370 %,<br> Temperature 302 °F
 ISO 11403-1 -2
18.68 MPa
<br>@Strain 0.400 %,<br> Temperature 90.0 °C
 2709 psi
<br>@Strain 0.400 %,<br> Temperature 194 °F
 ISO 11403-1 -2
24.27 MPa
<br>@Strain 0.360 %,<br> Temperature 40.0 °C
 3520 psi
<br>@Strain 0.360 %,<br> Temperature 104 °F
 ISO 11403-1 -2
28.72 MPa
<br>@Strain 1.24 %,<br> Temperature 150 °C
 4165 psi
<br>@Strain 1.24 %,<br> Temperature 302 °F
 ISO 11403-1 -2
35.72 MPa
<br>@Strain 0.440 %,<br> Temperature 23.0 °C
 5181 psi
<br>@Strain 0.440 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
38.12 MPa
<br>@Strain 0.420 %,<br> Temperature 0.000 °C
 5529 psi
<br>@Strain 0.420 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
38.53 MPa
<br>@Strain 2.20 %,<br> Temperature 150 °C
 5588 psi
<br>@Strain 2.20 %,<br> Temperature 302 °F
 ISO 11403-1 -2
41.17 MPa
<br>@Strain 1.10 %,<br> Temperature 90.0 °C
 5971 psi
<br>@Strain 1.10 %,<br> Temperature 194 °F
 ISO 11403-1 -2
44.43 MPa
<br>@Strain 3.16 %,<br> Temperature 150 °C
 6444 psi
<br>@Strain 3.16 %,<br> Temperature 302 °F
 ISO 11403-1 -2
53.57 MPa
<br>@Strain 6.46 %,<br> Temperature 150 °C
 7770 psi
<br>@Strain 6.46 %,<br> Temperature 302 °F
 ISO 11403-1 -2
55.58 MPa
<br>@Strain 0.920 %,<br> Temperature 40.0 °C
 8061 psi
<br>@Strain 0.920 %,<br> Temperature 104 °F
 ISO 11403-1 -2
55.85 MPa
<br>@Strain 1.87 %,<br> Temperature 90.0 °C
 8100 psi
<br>@Strain 1.87 %,<br> Temperature 194 °F
 ISO 11403-1 -2
62.8 MPa
<br>@Strain 0.660 %,<br> Temperature -20.0 °C
 9110 psi
<br>@Strain 0.660 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
64.86 MPa
<br>@Strain 2.72 %,<br> Temperature 90.0 °C
 9407 psi
<br>@Strain 2.72 %,<br> Temperature 194 °F
 ISO 11403-1 -2
68.1 MPa
<br>@Strain 0.880 %,<br> Temperature 23.0 °C
 9880 psi
<br>@Strain 0.880 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
75.05 MPa
<br>@Strain 1.44 %,<br> Temperature 40.0 °C
 10890 psi
<br>@Strain 1.44 %,<br> Temperature 104 °F
 ISO 11403-1 -2
84.36 MPa
<br>@Strain 0.960 %,<br> Temperature 0.000 °C
 12240 psi
<br>@Strain 0.960 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
88.7 MPa
<br>@Strain 1.99 %,<br> Temperature 40.0 °C
 12900 psi
<br>@Strain 1.99 %,<br> Temperature 104 °F
 ISO 11403-1 -2
89.21 MPa
<br>@Strain 1.26 %,<br> Temperature 23.0 °C
 12940 psi
<br>@Strain 1.26 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
99.12 MPa
<br>@Strain 1.01 %,<br> Temperature -40.0 °C
 14380 psi
<br>@Strain 1.01 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
107.95 MPa
<br>@Strain 1.72 %,<br> Temperature 23.0 °C
 15657 psi
<br>@Strain 1.72 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
109.81 MPa
<br>@Strain 1.33 %,<br> Temperature 0.000 °C
 15927 psi
<br>@Strain 1.33 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
111.73 MPa
<br>@Strain 1.23 %,<br> Temperature -20.0 °C
 16205 psi
<br>@Strain 1.23 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
132.69 MPa
<br>@Strain 1.77 %,<br> Temperature 0.000 °C
 19245 psi
<br>@Strain 1.77 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
140.62 MPa
<br>@Strain 1.49 %,<br> Temperature -40.0 °C
 20395 psi
<br>@Strain 1.49 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
147.79 MPa
<br>@Strain 1.77 %,<br> Temperature -20.0 °C
 21435 psi
<br>@Strain 1.77 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
169.84 MPa
<br>@Strain 2.23 %,<br> Temperature -20.0 °C
 24633 psi
<br>@Strain 2.23 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
170.93 MPa
<br>@Strain 1.91 %,<br> Temperature -40.0 °C
 24791 psi
<br>@Strain 1.91 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
197.31 MPa
<br>@Strain 2.38 %,<br> Temperature -40.0 °C
 28617 psi
<br>@Strain 2.38 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
Elongation at Break 3.5 %
3.5 %
ISO 527-1/-2
Tensile Modulus 8.50 GPa
1230 ksi
ISO 527-1/-2
3.672 GPa
<br>@Temperature 120 °C
 532.6 ksi
<br>@Temperature 248 °F
 ISO 11403-1 -2
6.643 GPa
<br>@Temperature 40.0 °C
 963.5 ksi
<br>@Temperature 104 °F
 ISO 11403-1 -2
9.965 GPa
<br>@Temperature -40.0 °C
 1445 ksi
<br>@Temperature -40.0 °F
 ISO 11403-1 -2
Flexural Strength 200 MPa
29000 psi
ISO 178
Flexural Modulus 7.70 GPa
1120 ksi
ISO 178
Shear Modulus 0.7794 GPa
<br>@Temperature 100 °C
 113.0 ksi
<br>@Temperature 212 °F
 Dynamic; ISO 11403-1 -2
1.256 GPa
<br>@Temperature 60.0 °C
 182.2 ksi
<br>@Temperature 140 °F
 Dynamic; ISO 11403-1 -2
1.966 GPa
<br>@Temperature 10.0 °C
 285.1 ksi
<br>@Temperature 50.0 °F
 Dynamic; ISO 11403-1 -2
2.137 GPa
<br>@Temperature -40.0 °C
 310.0 ksi
<br>@Temperature -40.0 °F
 Dynamic; ISO 11403-1 -2
2.331 GPa
<br>@Temperature -70.0 °C
 338.1 ksi
<br>@Temperature -94.0 °F
 Dynamic; ISO 11403-1 -2
2.501 GPa
<br>@Temperature -100 °C
 362.7 ksi
<br>@Temperature -148 °F
 Dynamic; ISO 11403-1 -2
Secant Modulus 2.95 GPa
<br>@Strain 3.47 %,<br> Temperature 40.0 °C
 428 ksi
<br>@Strain 3.47 %,<br> Temperature 104 °F
 ISO 11403-1 -2
3.97 GPa
<br>@Strain 2.41 %,<br> Temperature 40.0 °C
 575 ksi
<br>@Strain 2.41 %,<br> Temperature 104 °F
 ISO 11403-1 -2
4.95 GPa
<br>@Strain 1.62 %,<br> Temperature 40.0 °C
 717 ksi
<br>@Strain 1.62 %,<br> Temperature 104 °F
 ISO 11403-1 -2
5.47 GPa
<br>@Strain 2.90 %,<br> Temperature 0.000 °C
 794 ksi
<br>@Strain 2.90 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
5.71 GPa
<br>@Strain 2.05 %,<br> Temperature 23.0 °C
 828 ksi
<br>@Strain 2.05 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
6.0413 GPa
<br>@Strain 0.920 %,<br> Temperature 40.0 °C
 876.23 ksi
<br>@Strain 0.920 %,<br> Temperature 104 °F
 ISO 11403-1 -2
6.74 GPa
<br>@Strain 0.360 %,<br> Temperature 40.0 °C
 978 ksi
<br>@Strain 0.360 %,<br> Temperature 104 °F
 ISO 11403-1 -2
6.8305 GPa
<br>@Strain 1.41 %,<br> Temperature 23.0 °C
 990.70 ksi
<br>@Strain 1.41 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
6.95 GPa
<br>@Strain 2.08 %,<br> Temperature 0.000 °C
 1010 ksi
<br>@Strain 2.08 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2