Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 11.0 - 14.0 GPa | 1600 - 2030 ksi | Injection; ISO 178 |
Raschig Group 5562 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
Flexural Modulus | 11.0 - 14.0 GPa | 1600 - 2030 ksi | Compression; ISO 178 |
Raschig Group DECAL® 572R Phenolic Glass-fiber reinforced phenolic molding compound. Exceptional heat resistance with regard to maintaining surface finish and mechanical properties, outstanding mechanical properties, excellent rotati.. |
|||
Flexural Modulus | 2.41 - 14.0 GPa | 350 - 2030 ksi | Average value: 4.13 GPa Grade Count:47 |
Overview of materials for Polyetheretherketone, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, PTFE Filled". Each property range of values reported is minimum and maximum values.. |
|||
Flexural Modulus | 5.00 - 14.0 GPa @Temperature -40.0 - 121 °C |
725 - 2030 ksi @Temperature -40.0 - 250 °F |
Average value: 8.45 GPa Grade Count:8 |
Overview of materials for Nylon 66, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. .. |
|||
Flexural Modulus | 12.0 - 14.0 GPa | 1740 - 2030 ksi | ISO 178 |
Vyncolit G885 Novolac Phenolic Glass fiber and mineral filled phenolic molding compound with excellent mechanical and thermal properties. Information provided by Vyncolit, a Sumitomo Bak Group |
|||
Flexural Modulus | 12.0 - 14.0 GPa | 1740 - 2030 ksi | ISO 178 |
Vyncolit X658 Novolac Phenolic Glass fiber and mineral filled phenolic molding compound with excellent mechanical and thermal properties and a very good dimensional stability.USES: Complex precision parts.Information provided by .. |
|||
Flexural Modulus | 10.0 - 14.0 GPa | 1450 - 2030 ksi | ISO 178 |
Bulk Molding Compounds tetra-DUR L 4305 Bulk Molding Compound UL-licensed. Anchor wave-isolation.Typical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipation (explosion prote.. |
|||
Flexural Modulus | 10.0 - 14.0 GPa | 1450 - 2030 ksi | ISO 178 |
Bulk Molding Compounds tetra-DUR N 4303 Bulk Molding Compound Mechanical high grade standard product.Typical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipation (explosion p.. |
|||
Flexural Modulus | 11.0 - 14.0 GPa | 1600 - 2030 ksi | ISO 178 |
Vyncolit X682 Novolac Phenolic Glass fiber, glass bead and graphite filled phenolic molding compound with excellent mechanical properties and a low coefficient of friction.USES: Water pump seals and self-lubricating bearings.Info.. |
|||
Flexural Modulus | 12.0 - 14.0 GPa | 1740 - 2030 ksi | Injection; ISO 178 |
Raschig Group DECAL® 152CL Phenolic Glass-fiber and mineral reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This product meet.. |