Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 9.32 GPa | 1350 ksi | ASTM D790 |
Mitsui AURUM® JGN6230 Thermoplastic Polyimide Resin, Amorphous
(discontinued **) AURUM® is an easy melt, processable and recyclable thermoplastic polyimide resin that provides continuous service temperatures to 465° F in its amorphous state and up to 550° F when annealed to i.. |
|||
Flexural Modulus | 9.32 GPa @Temperature 150 °C |
1350 ksi @Temperature 302 °F |
ASTM D790 |
Mitsui AURUM® JGN6230 Thermoplastic Polyimide Resin, Crystalline
(discontinued **) AURUM® is an easy melt, processable and recyclable thermoplastic polyimide resin that provides continuous service temperatures to 465° F in its amorphous state and up to 550° F when annealed to i.. |
|||
Flexural Modulus | 9.32 GPa @Thickness 3.20 mm |
1350 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID GP2330B(W) PA66+GF33%, General Purpose Feature: Injection Molding, PA6+GF33%, General PurposeApplication: Automotive (Air Intake Manifold, Cylinder Head Cover)CAS No. 32131-17-2 and 65997-17-3Information provided by LG Chemical |
|||
Flexural Modulus | 9.32 GPa @Thickness 3.20 mm |
1350 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUMID GP2330BL PA66+GF33%, General Purpose Feature: Injection Molding, PA66+GF33%, General PurposeApplication: Automotive (Radiator Tank, Reservoir)Information provided by LG Chemical |
|||
Flexural Modulus | 9.32 GPa | 1350 ksi | DIN 53452; ASTM D790 |
Kolon KOPA® KN333G33BL G/F Reinforced Nylon 66 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstandin.. |
|||
Flexural Modulus | 9.32 GPa @Thickness 3.20 mm |
1350 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
LG Chemical LUSEP SP2306F SPS+GF30%, Flame Retardant Feature: Injection Molding, sPS+GF30%, Flame RetardantApplication: Pump Units, Pick-up Lends Holder, etcCAS No. 9003-53-6, 68928-70-1, 1309-64-4 and 65997-17-3Information provided by LG Chemical |
|||
Flexural Modulus | 9.32 GPa | 1350 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM SF2350 PEI Blend High flow Ultem blends for thin wall application |
|||
Flexural Modulus | 9.32 GPa | 1350 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics ULTEM SF2350 PEI Blend (Asia Pacific) High flow Ultem blends for thin wall application |
|||
Flexural Modulus | 9.32 GPa | 1350 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Ultem SF2350 PEI Blend (Europe-Africa-Middle East) High flow Ultem blends for thin wall applicationThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Flexural Modulus | 9.32 GPa | 1350 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® AR-5300H PBT/ASA, 30% Glass Filled Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 9.32 GPa | 1350 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® AR-9301 PA, Glass Filled General Purpose Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 9.32 GPa | 1350 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® EM-8240C MPPE, Glass Filled MPPE/GF material that is used in the main frame of banknote sortersInformation provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 9.32 GPa | 1350 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® AR-5300H PBT/ASA, 30% Glass Filled Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 9.32 GPa | 1350 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® AR-9301 PA, Glass Filled General Purpose Information provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 9.32 GPa | 1350 ksi | 2.8 mm/min; ASTM D790 |
Samsung Cheil Industries Infino® EM-8240C MPPE, Glass Filled MPPE/GF material that is used in the main frame of banknote sortersInformation provided by Samsung Cheil Industries. |
|||
Flexural Modulus | 9.32 GPa | 1350 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP RF007ES PA 66 LNP* THERMOCOMP* RF007ES is a compound based on Nylon 66 resin containing 35% Glass Fiber. Added features of this material include: Heat Stabilized, Easy Molding. |
|||
Flexural Modulus | 9.32 GPa | 1350 ksi | ASTM D790 |
Shinkong Synthetic Fibers Shinite® D202G30 PBT, 30% Glass Filled, Fire Retardant Information from Shinkong Synthetic Fibers Corp. |
|||
Flexural Modulus | 9.32 GPa | 1350 ksi | ASTM D790 |
Shinkong Synthetic Fibers Shinite® D202G30 PBT, 30% Glass Filled, Fire Retardant Information from Shinkong Synthetic Fibers Corp. |
|||
Flexural Modulus | 9.32 - 17.0 GPa | 1350 - 2470 ksi | Average value: 13.3 GPa Grade Count:18 |
Overview of materials for Polyethylene Terephthalate (PET), 50% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 50% Glass Reinforced". Specific grades with glass content between 45% .. |
|||
Flexural Modulus | 9.32 GPa | 1350 ksi | ASTM D790 |
Samyang Tripet® 2500G45 Polyethylene Terephthalate, 45% Glass Fiber Reinforced TRIPET® has excellent heat resistance, good surface, chemical resistance and high electrical performance.Applications:Coil BobbinConnectorMotor HousingLamp HousingRelay BaseIron bodyAll information.. |