- Samsung Cheil Industries Infino® AR-5300H PBT/ASA, 30% Glass Filled
Samsung Cheil Industries Infino® AR-5300H PBT/ASA, 30% Glass Filled
| Category | Polymer , Thermoplastic , ASA Polymer , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + ASA Blend, Glass Fiber Reinforced |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® AR-5300H PBT/ASA, 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.20 mm |
0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 3.20 mm |
0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 30 g/10 min @Load 5.00 kg, Temperature 250 °C |
30 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength at Break | 127 MPa | 18400 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 132 MPa | 19200 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 8.83 GPa | 1280 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 186 MPa | 27000 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 9.32 GPa | 1350 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.686 J/cm @Thickness 6.35 mm |
1.29 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 0.785 J/cm @Thickness 3.17 mm |
1.47 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C @Thickness 6.40 mm |
401 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C @Thickness 6.40 mm |
374 °F @Thickness 0.252 in |
ASTM D648 |
Users viewing this material also viewed the following:
- ExxonMobil Exceed™ 1012CA Film Resin (discontinued **)
- Kinlead HSS12 Normal Grade Heat Sealable Film (thickness: 30 µm)
- Michelman® Michem® Wood Coating 70M Anionic paraffin blend emulsion
- A. Schulman SCHULAMID® 6 MV5 Unreinforced Nylon 6
- A. Schulman PP 3353-01 Polypropylene Medium Impact Polypropylene
- Elektro-Isola Etronit IIQ S Phenolic, Paper Reinforcement, Black, Sheets
- Solvay Specialty Polymers Amodel® AT-1001L Polyphthalamide (PPA) (Unverified Data**)
- Plenco 50335 PET, Pellet, Injection Molded, White (discontinued **)
Copyright © lookpolymers.com All Rights Reserved