SABIC Innovative Plastics ULTEM SF2350 PEI Blend (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM SF2350 PEI Blend (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow Ultem blends for thin wall application
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ISO 62-1 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH |
| Melt Flow | 14.7 g/10 min @Load 6.60 kg, Temperature 337 °C |
14.7 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Melt Index of Compound | 30 g/10 min @Load 10.0 kg, Temperature 345 °C |
30 g/10 min @Load 22.0 lb, Temperature 653 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 171 MPa | 24800 psi | 5 mm/min; ISO 527 |
| 172 MPa | 24900 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 11.6 GPa | 1680 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 222 MPa | 32200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 9.32 GPa | 1350 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 9.40 GPa | 1360 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.950 J/cm | 1.78 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.0 µm/m-°C @Temperature 23.0 - 150 °C |
7.78 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| 15.0 µm/m-°C @Temperature -40.0 - 150 °C |
8.33 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature -40.0 - 150 °C |
30.6 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 56.0 µm/m-°C @Temperature 23.0 - 150 °C |
31.1 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 209 °C | 408 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 204 °C @Thickness 3.20 mm |
399 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Hexion Bakelite™ X24 Phenolic Formaldehyde Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 1105/GF/30/NAT-2 PEEK, with glass fiber
- SABIC Innovative Plastics LNP LUBRICOMP JFL36 PES (Asia Pacific)
- Schott Glass 8228 Intermediate sealing glass
- SABIC Innovative Plastics LNP Stat-kon WFD059 PBT
- DSM Akulon® K224-HG7 Nylon 6-35% Glass Reinforced (European Grade) (Cond)
- Chosun Refractories 1260BLANKET Blanket
- Colorite Polymers 7533 General Purpose Vinyl Compound
- ATI Allegheny Ludlum S7 Tool Steel, UNS T41907
Copyright © lookpolymers.com All Rights Reserved