Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 8.00 GPa | 1160 ksi | 1.3 mm/min; ASTM D790 |
Ovation Polymers RIGITRON 30525 GF FR PET, 25% Glass Reinforced PET – 25% Short Glass Fiber Reinforced with Flame retardant. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared according to AS.. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM D790 |
Premix Premi-Glas® 2200-15 CR-SX Fiberglass Reinforced SMC Description: Premi-Glas® 2200-15 CR-SX is a fiberglass reinforced thermoset Sheet Molding Compound formulated for excellent electrical properties and fire retardance; it also has very good thermal .. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM D790 |
Premix Premi-Glas® 2203-15 CR-SX-HT Fiberglass Reinforced Thermoset SMC Premi-Glas® 2203-15 CR-SX-HT is a fiberglass reinforced thermoset sheet molding compound for electrical and flame retardant applications.Key features and benefits are:Enhanced product for higher UL.. |
|||
Flexural Modulus | 8.00 GPa @Temperature 23.0 °C |
1160 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PPH GF5030 HC Polypropylene Homopolymer, Glass Fibre-Reinforced Information provided by Polykemi AB |
|||
Flexural Modulus | 8.00 - 12.0 GPa | 1160 - 1740 ksi | Compression; ISO 178 |
Raschig Group 2568 AMC Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for s.. |
|||
Flexural Modulus | 8.00 - 11.0 GPa | 1160 - 1600 ksi | Compression; ISO 178 |
Raschig Group 4552 Silicone Glass fiber reinforced silicone molding compound. Excellent thermal stability - up to +/- 300°C continuously, excellent electrical properties, good mechanical strength, very good dimensional stabi.. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM Data |
BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron HPN 9333G HS is a heat stabilized, 33% glass reinforced, impact modified polyamide 6 injection molding compound combining exceptional strength, stiffness and high temperature performance with.. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | ISO 178 |
Nilit FRIANYL A63 H-GV35 Nylon 6.6 for injection molding, 35% glass fiber reinforced Nylon 6.6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | |
Lehmann & Voss LUVOCOM® 20-8332 Polyphthalamide, with glass fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Low influence from moisture and temperature to measures and electrical prop.. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | |
Lehmann & Voss LUVOCOM® 3-7088-1 Polyamide 6, with carbon fiber and glass fiber, low-warpage Applications: Automotive industry, textile machinery, apparatus- and precision engineering.Strong, stiff parts.dynamic stressElectrically conductive, suitable for continuous discharging of staticall.. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM D790 |
Glastic Laminates/Shapes Polyester, Channels and Structural Shapes (GPO3) Data provided by Glastic Corporation.NEMA GPO-3. Average data - may vary with the size and shape of the electrical insulating structural product. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM D790 |
Loxim 330 01HB Nylon 6 Information provided by Loxim Industries |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | |
Lehmann & Voss LUVOCOM® 1/GF/30/TF/15 Polyamide 66, with glass fiber and PTFE, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.High dimensionally stable prec.. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | |
Lehmann & Voss LUVOCOM® 1/GF/30/TF/15/SI/2-2 Polyamide 66, with glass fiber, PTFE, lubricant modified, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.High dimensionally stable prec.. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | DIN 53457 |
Schwartz Technical Plastics MITELA® 2/5 A Cotton Fabric, Special Quality Application: bearing shells and bearing collarsInformation provided by Schwartz Technical Plastics GmbH |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® 830F PBT+PET (Asia Pacific) PBT+PET, 30% Glass, Mold Release, Heat Stabilized, For food contact applications |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL NH8006 PPE+HIPS (Europe-Africa-Middle East) Noryl* NH8006 resin is a 30% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve a UL94 V0 flame rating (color specific) while offering an exceptio.. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Stat-kon RE003 PA 66 (Europe-Africa-Middle East) LNP* Stat-kon* RE003 is a compound based on Nylon 66 resin containing Carbon Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP Thermocomp PF006 PA 6 (Europe-Africa-Middle East) 30% glass fibre reinforced Polyamide 6 injection moulding resin.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM-D790 |
Polyram PlusTek PA301G6 Nylon 6.6, Heat Stabilized, 30% Glass Fiber Heat stabilized, 30% glass fiber reinforced polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM-D790 |
Polyram PlusTek PA303G6 Nylon 6.6, Heat Stabilized, 30% Glass Fiber 30% glass fiber reinforced, heat stabilized and hydrolysis resistant polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | ISO 178-93 |
Wellman Wellpet® MRGF101-GY1 PET, 29% Mineral/Glass Fiber Reinforced Typical data obtained from injection molded test bars, tested dry as molded at 73°F (23°C). Information provided by Wellman, Inc. Engineering Resins Division. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | ISO 178 |
Polyram RamSter PF306G6 PBT, 30% Glass Fiber 30% Glass fiber reinforced, low viscosity PBT for injection molding applications.Information provided by Polyram. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM-D790 |
Toyobo VYLOPET® EMC320R Polyester Resin VYLOPET® is a polyester resin developed specifically for injection molding. Polyester resins have excellent heat resistance, rigidity, chemical resistance, and electric properties. Grade EMC320R ha.. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM-D790 |
Polyram PlusTek PB303G6 Nylon 6, 30% Glass Fiber 30% Glass-fiber reinforced, heat stabilized polyamide 6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM-D790 |
Polyram RamSter PF321G6 PBT, 30% Glass Fiber, Flame Retardant 30% Glass fiber reinforced, flame retardant PBT for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | ISO 178 |
Eurostar Starflam PF0057E PA6, 25% Glass Filled, Injection Molded Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Fiber Reinforced, Polyamide 6 Injection Molding Resin (also known as PF-1005 Z270)Information provided by Polymer Technology & Services,.. |
|||
Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM D790 |
BLUESTAR 201-G30202 PBT, 30% Glass Filled Typical Applications: Energy saving lighting, E/E applicationsInformation provided by Polymer Technology and Services, LLC (PTS). |