Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 3.45 GPa | 500 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® CM6140 PC+ABS (Europe-Africa-Middle East) Cycoloy resin grade CM6140 is a flame retardant, filled PC/ABS blend. It is of non-brominated & non-chlorinated FR system to meet UL94 V0 at 0.8mm. Key features include thin wall FR, higher stiffnes.. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | |
Quadrant EPP Ertacetal® H POM-H, extruded (ISO Data) Ertacetal H is Quadrant’s homopolymer acetal grade. It offers a higher mechanical strength, stiffness, hardness and creep resistance as well as a lower thermal expansion rate and often also a bette.. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | Conditioned; ASTM D790 |
Solvay Specialty Polymers Amodel® AT-6115 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AT-6115 HS is a 15% glass-fiber reinforced, toughened grade of polyphthalamide (PPA) resin designed to possess more elongation than other 15% glass-fiber reinforced grades of Amodel resin. Th.. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
Quadrant EPP Duratron® PEI U1000 Extruded Unfilled Polyetherimide (ASTM Product Data Sheet) |
|||
Flexural Modulus | 3.45 - 10.7 GPa | 500 - 1550 ksi | Average value: 5.66 GPa Grade Count:22 |
Overview of materials for Acetal Homopolymer, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, Glass Fiber Reinforced". Each property range of values reported is minimum and maxim.. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
Ravago Manufacturing Americas Hylon® N1040MGL Nylon 6/6 (Cond)
(discontinued **) Information provided by Ravago. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | 2.0 in/min; ASTM D790 |
LTL Color Compounds ColorFast® PCGF110 Polycarbonate, 10% Glass-Filled High modulus 10% glass-filled polycarbonate, V2-rated, general purposeAll information provided by LTL Color Compounders, Inc. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
Techmer ES Luriblend® PC GF10 TS15 BK 10% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 10% Filler by WeightAdditive: PTFE + Silicone Lubricant(15%)Features: LubricatedAppearance: BlackInformation provided by T.. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
Chi Mei Kibisan® PN107 SAN Resin, General Purpose Product CharacteristicsWater ClearHigh RigidityMedium FlowInformation provided by Calsak Corporation |
|||
Flexural Modulus | 3.45 GPa | 500 ksi | Tangent; ISO 178 |
A. Schulman FORMION™ FI 388 Ionomer Information provided by A. Schulman. |
|||
Flexural Modulus | 3.45 - 77.9 GPa | 500 - 11300 ksi | Average value: 16.1 GPa Grade Count:26 |
Overview of materials for Vinyl Ester Sheet Molding Compound This property data is a summary of similar materials in the MatWeb database for the category "Vinyl Ester Sheet Molding Compound". Each property range of values reported is minimum and maximum value.. |