Network Polymers SAN 290 High Flow Natural
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Transparent |
| Manufacturer | Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers SAN 290 High Flow Natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: SAN - Styrene Acrylonitrile Transparent Engineering ThermoplasticInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 31.1 g/10 min @Load 3.80 kg, Temperature 230 °C |
31.1 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 70 | 70 | ASTM D785 |
| Tensile Strength, Yield | 68.9 MPa | 10000 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 3.45 GPa | 500 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 0.214 J/cm | 0.400 ft-lb/in | 0.125 inch bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 91.1 °C | 196 °F | Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| Vicat Softening Point | 100 °C | 212 °F | 0.125 inch bar, 1 Kg; ASTM D1525 |
| Flammability, UL94 | HB | HB | 0.0625 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXE1112T PC Copolymer
- Lehmann & Voss LUVOCOM® 1105-8000 PEEK, with carbon fiber, lubricant modified
- A. Schulman POLYBATCH™ Blue 4500GZ Concentrate Based in Low-Density Polyethylene
- Cheng Yu Plastic N66C3 Nylon 66, 30% Mineral Reinforced
- Entec Hypro™ PPC-CC20 Natural Copolymer Polypropylene, 20% Calcium Carbonate Filled
- Arkema Group Cristamid® MS 1300 Semi-Aromatic Nylon (PASA) (Dry)
- BASF Sicotan® Yellow K 2011 Color Additive
- LATI LAESTRA G/40 40% Glass Fiber Reinforced Syndiotactic Polystyrene (SPS) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved