Ravago Manufacturing Americas Hylex® P1010G10FRMA Polycarbonate, 10% Glass Filled
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylex® P1010G10FRMA Polycarbonate, 10% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate, 10% Glass Filled, Flame RetardantInformation provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm @Thickness 3.17 mm |
0.0020 - 0.0050 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 83.0 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 |
| Flexural Modulus | 3.45 GPa | 500 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 290 °F | ASTM D648 |
| Vicat Softening Point | 154 °C | 310 °F | ASTM D1525 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| V-0 - 5VA @Thickness 3.00 mm |
V-0 - 5VA @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 16.9 kV/mm | 430 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- Huntsman PE1503 EVA Film Extrusion (discontinued **)
- KB Alloys Ticar® 3% Ti - 0.15% C Titanium Carbon Aluminum Rod
- Shin-Etsu Silicones KSG-326 Fluid
- ExxonMobil Bicor® 380 AB OPP Film
- Cyclewood Solutions Xylomer™ XM2-CUA Sustainable Injection Molding Resin
- DuPont Performance Polymers Zytel® 77G33HS1L NC010 Nylon 612
- Hippe MF GC 201 Woven Glass Cloth Reinforced Melamine Resin - Sheet
- Fainplast Compounds PH 60/A Flexible PVC, Transparent Extrusion
- Teijin Panlite® G-3420R Glass Fiber Reinforced Polycarbonate Resin
Copyright © lookpolymers.com All Rights Reserved