Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 1.98 GPa | 287 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers UTTAP ES 10559 Polycarbonate Alloy Polycarbonate Alloy – High temperature (HDT), high Impact, with excellent short and long term heat stability. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative h.. |
|||
Flexural Modulus | 1.98 GPa | 287 ksi | ASTM D790-1 |
Ineos Styrenics 473D High-Impact Polystyrene Resin (NAFTA) Description: High-impact, high-flow grade for a wide variety of applications, including appliance components, consumer electronics housings, magnetic and optical media, building and construction, pa.. |
|||
Flexural Modulus | 1.98 GPa | 287 ksi | |
Kuraray SEPTON® CM2 Compatibilizer Description: SEPTON® is a series of high performance thermoplastic rubbers developed by Kuraray Co. Ltd. using its isoprene technology. SEPTON® resins are a series of hydrogenated styrenic blo.. |
|||
Flexural Modulus | 1.98 GPa | 287 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-KON SD000 PA12 LNP* STAT-KON* SD000 is an unfilled Nylon 12 compound. Added feature of this grade is: Electrically Conductive. |
|||
Flexural Modulus | 1.98 GPa | 287 ksi | ISO 178 |
SABIC Innovative Plastics LNP STAT-LOY A3000 ABS LNP STAT-LOY* A3000 is a compound based on ABS resin. Added feature of this material is: Antistatic. |
|||
Flexural Modulus | 1.98 GPa | 287 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP STAT-LOY A3000 ABS (Asia Pacific) LNP STAT-LOY A3000 is a compound based on Acrylonitrile butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistatic. Also known as: STAT-LOY A |
|||
Flexural Modulus | 1.98 GPa | 287 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp YF005 LNP* Thermocomp* YF005 is a compound based on TPEE resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Modulus | 1.98 GPa | 287 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP YF005 POLYESTER ELASTOMER LNP* THERMOCOMP* YF005 is a compound based on Polyester Elastomer resin containing 25% Glass Fiber. |
|||
Flexural Modulus | 1.98 GPa | 287 ksi | ISO 178 |
Lubrizol Isoplast® 300 Engineering Thermoplastic Polyurethane Resin Type: Isoplast® 300 is an engineering thermoplastic polyurethane resin.Appearance: Clear transparent pelletsApplication: Sheet extrusion, composite structures for industrial and consumer goods, inj.. |
|||
Flexural Modulus | 1.98 GPa | 287 ksi | ISO 178 |
DSM Fibre Intermediates Nyrim® 1525 (Glass), Conditioned Conditioned at 23°C and 50% Relative Humidity.Nyrim is a Block Copolymer of Nylon 6 and an elastomer with exceptional properties in impact resistance, fatigue and abrasion resistance. Nyrim is proc.. |
|||
Flexural Modulus | 1.98 GPa | 287 ksi | conditioned 15 days, 23°C - 50 % R.H.; ISO 178 |
Arkema Group Rilsan® Clear G170 Polyamide Rilsan® Clear G170 is a high performance transparent polyamide with outstanding thermal resistance. This grade has been designed for extrusion and injection molding applications and for medical use.. |
|||
Flexural Modulus | 1.98 GPa @Thickness 3.20 mm |
287 ksi @Thickness 0.126 in |
5.1mm/min; ASTM D790 |
Styron Magnum™ 1150 EM Acrylonitrile Butadiene Styrene (ABS) Overview: MAGNUM™ ABS resins are thermoplastic materials which provide an excellent balance to processability, impact resistance and heat resistance as imparted by the various polymer compositions... |