Ineos Styrenics 473D High-Impact Polystyrene Resin (NAFTA)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Ineos Styrenics |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Styrenics 473D High-Impact Polystyrene Resin (NAFTA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: High-impact, high-flow grade for a wide variety of applications, including appliance components, consumer electronics housings, magnetic and optical media, building and construction, packaging and food service, recreation equipment and sporting goods, medical devices and labware, office products, cosmetic and personal care products, and housewares.Information provided by BASF.Ineos Styrenics purchased this product line from BASF in 2005.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Water Absorption at Saturation | <= 0.10 % | <= 0.10 % | |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 13 g/10 min @Load 5.00 kg, Temperature 200 °C |
13 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 16.0 MPa | 2320 psi | ASTM D638 |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Tensile Modulus | 2.275 GPa | 330.0 ksi | ASTM D638 |
| Flexural Modulus | 1.98 GPa | 287 ksi | ASTM D790-1 |
| Izod Impact, Notched | 1.12 J/cm | 2.10 ft-lb/in | ASTM D256-A |
| Gardner Impact | 28.2 J @Temperature 23.0 °C |
20.8 ft-lb @Temperature 73.4 °F |
ASTM D5420, GB |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 81.1 °C | 178 °F | ASTM D648 |
| Vicat Softening Point | 93.3 °C | 200 °F | ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
Natural Color |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 55 % | 55 % | 60°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 280 °C | 356 - 536 °F | Injection Molding |
Users viewing this material also viewed the following:
- Reade Advanced Materials Gallium Nitrate (Ga(NO3)3·XH2O )
- Technetics Group Amicon™ Nylon 6/66 (Unverified Data**)
- LG Chemical LUPOY GN1002FC PC, Halogen Free, Flame Retardant, High Impact
- Inno-Comp INNOPOL® CS 1-5140 BLH 40% Talc-Filled Polypropylene Homopolymer
- Goodfellow Magnetic Copper Alloy
- Dow Corning 7-3100 GUM BLEND HIP EMULSION
- Dow CYCLOTENE™ XU35133 Advanced Electronic Resins (PhotoBisbenzocyclobutene BCB)
- 3M 41826 Industrial Polyethylene Temporary Surface Protection Tape
- 3M 3903 Vinyl Duct Tape
Copyright © lookpolymers.com All Rights Reserved