SABIC Innovative Plastics LNP THERMOCOMP YF005 POLYESTER ELASTOMER
| Category | Polymer , Thermoplastic , Polyester, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP YF005 POLYESTER ELASTOMER.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* YF005 is a compound based on Polyester Elastomer resin containing 25% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.310 % | 0.310 % | 50% RH, 24 hrs; ASTM D570 |
| 0.410 % | 0.410 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 5 mm/min; ISO 527 |
| 46.0 MPa | 6670 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | 5 mm/min; ISO 527 |
| 47.0 MPa | 6820 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 8.3 % | 8.3 % | Type I, 5 mm/min; ASTM D638 |
| 10.3 % | 10.3 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 9.5 % | 9.5 % | 5 mm/min; ISO 527 |
| 9.9 % | 9.9 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.36 GPa | 342 ksi | 1 mm/min; ISO 527 |
| 2.37 GPa | 344 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 53.0 MPa | 7690 psi | ISO 178 |
| Flexural Modulus | 1.98 GPa | 287 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.12 GPa | 307 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 3.31 J/cm | 6.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.98 J/cm | 18.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 76.0 kJ/m² | 36.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 15.0 J @Temperature 23.0 °C |
11.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 7.00 J | 5.16 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
20.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 177 µm/m-°C @Temperature -30.0 - 30.0 °C |
98.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 186 °C @Thickness 3.20 mm |
367 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 142 °C | 288 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 152 °C @Thickness 3.20 mm |
306 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Osprey Metals 85/15 Cu Sn Powder (Grade 90% - 22)
- Shandong Rike Chemical HELIâ„¢ HL-275D PVC Processing Aid Series (PA)
- Struktol STRUKSILON 8002 Silicone Stabilizer for PU-Rigid Foam
- Master Bond EP21SC-1 Two Component Epoxy Resin System
- DSM Akulon® K224-PG3 Impact Modified Nylon 6-15% Glass Reinforced (European Grade) (Dry)
- Covestro Makrolon® 1899* Polycarbonate, Impact Grade
- CP-Polymer-Technik Wellamid® 6600 MR 209 HWCP 20% Mineral Nylon 66, Heat Stabilized, Conditioned
- China Tungsten FeMo60-B Ferro Molybdenum
- BASF Novolen® 1100 RC Polypropylene, Injection Molding Grade
- BASF 2-Mercaptoethanol
Copyright © lookpolymers.com All Rights Reserved