Styron Magnum™ 1150 EM Acrylonitrile Butadiene Styrene (ABS)

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Styron
Trade Name Magnum™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron Magnum™ 1150 EM Acrylonitrile Butadiene Styrene (ABS).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: MAGNUM™ ABS resins are thermoplastic materials which provide an excellent balance to processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ABS resin are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming processes. The automotive grades of MAGNUM ABS resins offer a wide range of gloss, viscosities, impact strength and heat properties fo ruse in numerous automotive applications. Melt flow rates from 1 to 12 g/10 min, impact strengths from 2.5 to 12 ft-lb/in and heat distortion temperatures from 165 to 190° F are available. Available primarily as natural plus concentrates, MAGNUM ABS resins are used in a wide variety of automotive applications including structural instrument panels, consoles, pillars and exterior trim parts requiring painting and plating. Within the MAGNUM ABS product line, MAGNUM 1150 EM ABS resin is a high impact, medium heat, low gloss resin. MAGNUM 1150 EM has improved low temperature impact strength over standard grades of ABS. MAGNUM 1150 EM is used in applications like pillars and instrument panel trim. Information provided by StyronThis product line was spun off from Dow Chemical to Styron in 2010.
Physical Properties Metric English Comments
Specific Gravity 1.03 g/cc
1.03 g/cc
ASTM D792
Maximum Moisture Content 0.10
0.10
Linear Mold Shrinkage, Flow 0.0060 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0060 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 0.90 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 0.90 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 36.5 MPa

@Thickness 3.20 mm
 5290 psi

@Thickness 0.126 in
 51mm/min; ASTM D638
Elongation at Break 30 %

@Thickness 3.20 mm
 30 %

@Thickness 0.126 in
 51mm/min; ASTM D638
Elongation at Yield 3.0 %

@Thickness 3.20 mm
 3.0 %

@Thickness 0.126 in
 51mm/min; ASTM D638
Tensile Modulus 1.75 GPa

@Thickness 3.20 mm
 254 ksi

@Thickness 0.126 in
 51mm/min; ASTM D638
Flexural Strength 58.9 MPa

@Thickness 3.20 mm
 8540 psi

@Thickness 0.126 in
 5.1mm/min; ASTM D790
Flexural Modulus 1.98 GPa

@Thickness 3.20 mm
 287 ksi

@Thickness 0.126 in
 5.1mm/min; ASTM D790
Izod Impact, Notched 3.40 J/cm

@Thickness 3.20 mm,
Temperature -29.0 °C
 6.37 ft-lb/in

@Thickness 0.126 in,
Temperature -20.2 °F
 ASTM D256
5.60 J/cm

@Thickness 32.0 mm,
Temperature 23.0 °C
 10.5 ft-lb/in

@Thickness 1.26 in,
Temperature 73.4 °F
 ASTM D256
Dart Drop, Total Energy 29.9 J

@Thickness 3.20 mm,
Temperature 23.0 °C
 22.1 ft-lb

@Thickness 0.126 in,
Temperature 73.4 °F
 6.71 m/sec, Peak Energy; ASTM D3763
32.8 J

@Thickness 3.20 mm,
Temperature -29.0 °C
 24.2 ft-lb

@Thickness 0.126 in,
Temperature -20.2 °F
 6.71 m/sec, Peak Energy; ASTM D3763
42.9 J

@Thickness 3.20 mm,
Temperature -29.0 °C
 31.6 ft-lb

@Thickness 0.126 in,
Temperature -20.2 °F
 6.71 m/sec, Total Energy; ASTM D3763
45.2 J

@Thickness 3.20 mm,
Temperature 23.0 °C
 33.3 ft-lb

@Thickness 0.126 in,
Temperature 73.4 °F
 6.71 m/sec, Total Energy; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 0.950 µm/m-°C

@Thickness 3.20 mm
 0.528 µin/in-°F

@Thickness 0.126 in
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 96.1 °C

@Thickness 3.20 mm
 205 °F

@Thickness 0.126 in
 Unannealed; ASTM D648
111 °C

@Thickness 3.20 mm
 232 °F

@Thickness 0.126 in
 Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 82.2 °C

@Thickness 3.20 mm
 180 °F

@Thickness 0.126 in
 Unannealed; ASTM D648
108 °C

@Thickness 3.20 mm
 226 °F

@Thickness 0.126 in
 Annealed; ASTM D648
Vicat Softening Point 112 °C
234 °F
ASTM D1525
Processing Properties Metric English Comments
Melt Temperature 218 - 274 °C
424 - 525 °F
Mold Temperature 26.7 - 60.0 °C
80.1 - 140 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Back Pressure 1.03 - 3.45 MPa
149 - 500 psi
Descriptive Properties Value Comments
Clamp Tonnage 2.8-6.9 kN/cm2
Screw Compression Ratio 1.5:1 to 3.5:1
Screw L/D Ratio 20:1
Users viewing this material also viewed the following: