SABIC Innovative Plastics LNP STAT-KON SD000 PA12
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON SD000 PA12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* SD000 is an unfilled Nylon 12 compound. Added feature of this grade is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Density | 1.124 g/cc | 0.04061 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.150 % | 0.150 % | 50% RH, 24 hrs; ASTM D570 |
| 0.210 % | 0.210 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | Type I, 5 mm/min; ASTM D638 |
| 44.0 MPa | 6380 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | 5 mm/min; ISO 527 |
| 51.0 MPa | 7400 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 17.1 % | 17.1 % | 5 mm/min; ISO 527 |
| 28.1 % | 28.1 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 11.3 % | 11.3 % | 5 mm/min; ISO 527 |
| 13.4 % | 13.4 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.10 GPa | 305 ksi | 1 mm/min; ISO 527 |
| 2.21 GPa | 321 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 67.0 MPa | 9720 psi | ISO 178 |
| Flexural Modulus | 1.98 GPa | 287 ksi | 2 mm/min; ISO 178 |
| 2.05 GPa | 297 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.350 J/cm | 0.656 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 19.1 J/cm | 35.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 219 kJ/m² | 104 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 2.00 J @Temperature 23.0 °C |
1.48 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 99.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
55.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 108 µm/m-°C @Temperature -30.0 - 30.0 °C |
60.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 158 °C @Thickness 3.20 mm |
316 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 61.0 °C | 142 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 96.0 °C @Thickness 3.20 mm |
205 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.0 - 4.0 ohm | 1.0 - 4.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Nabaltec NABALOX® NO 713-10 MF Reactive Alumina
- Pasargad Polymer Peyvand Pasalen 3P-H3520B Polypropylene, 20% EPDM Filled
- Flint Hills AP5106-HA Polypropylene Impact Copolymer
- Haveg Havaflex T.A.-117 Phenolic, Trowelable Ablative Coating
- ExxonMobil Solvesso™ 100 Aromatic Fluid
- ExxonMobil Vistalon™ 2502 Ethylene Propylene Diene Terpolymer Rubber
- E-Polymers TEKAMID® TA250GFR , Flame Retardant, 25% Glass Fiber Reinforced PA66, DAM
- Eurostar Staramide RB008 PA66, 40% Glass Bead Filled, Injection Molded
- 3M Scotch® 690 Colored Film Tape
- C.O.I.M. FILCO® 656 Unsaturated Polyester Powder Resin
Copyright © lookpolymers.com All Rights Reserved