Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 1.80 GPa | 261 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
Ovation Polymers Opnyl OP66UT119 Nylon 66 Ultra Tough - High Impact, Excellent retention of mechanical properties, High service temperature. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All.. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 |
SABIC Innovative Plastics LNP COLORCOMP M1000S PP LNP COLORCOMP* M1000S is an unfilled Polypropylene resin. Added features of this material include: Heat Stabilized. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | 2mm/min; ASTM D790 |
3M Dyneon™ PVDF 6020/1001 Polyvinylidene Fluoride
(discontinued **) Ultra-high molecular weight grade PVDFPowder gradeExcellent chemical resistance to a wide variety of aggressive fluids and solventsGood permeation resistanceExcellent strength and dimensional stabil.. |
|||
Flexural Modulus | 1.80 - 9.00 GPa | 261 - 1310 ksi | Average value: 4.94 GPa Grade Count:10 |
Overview of materials for Nylon 6, Mineral Reinforced, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Mineral Reinforced, Impact Grade". Each property range of values reported is minimum and maximu.. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | |
Lehmann & Voss LUVOCOM® 1850-8197 PBT, lubricant modified, easy flowing, demolding aid Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Parts for electric and electro.. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | |
Lehmann & Voss LUVOCOM® 50/TF/15/GY04 Polycarbonate, with PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Improved friction and wear behaviour. Emergency running proper.. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | |
Lehmann & Voss LUVOCOM® 80/TF/18/SI/2/BK Polyacetal-copolymer, with PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, gl.. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | |
Lehmann & Voss LUVOCOM® 80-8318-1 Polyacetal-copolymer, with PTFE, easy flowing Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, gl.. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 |
Grupo Repol Dinalon® B3S25 PA6 Unreinforced Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 |
Solvay Technyl® A 246M Nylon 66, Impact Grade, EH0 Unreinforced and modified polyamide 66, with improved impact resistance, heat stabilized, for injection molding.Technyl A 246m offers an excellent notched impact resistance at low temperatures makin.. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 |
Solvay Technyl® C 206 Nylon 6, EH0 Unreinforced Plyamide PA6, standard for fast cycling, for injection molding.Technyl C 206 has high fluidity and good mold release, favored by a high crystallization rate. It is specially suitable f.. |
|||
Flexural Modulus | 1.80 GPa @Temperature 260 °C |
261 ksi @Temperature 500 °F |
ASTM D790 |
Saint-Gobain Meldin® 7021 Direct Formed Graphite Filled Polyimide Finished parts and basic shapes made from 15% by weight graphite filled polyimide material for applications high wear resistance, good thermal oxidative stability, and high temperature resistance. .. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 |
A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene DescriptionPolyfort® FPP 1876 is a 22% mineral filled copolymer UV Inhibited Polypropylene. It is high flow. Information provided by A. Schulman. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 |
Wellman Wellamid® 22LHI4 XE-N Impact Modified Nylon 66, Lubricated & Heat Stabilized Typical Applications: Automotive fasteners, living hinge, head lamp adjustment devices, ink pen components, wire separators, hardware components, window installation clips, safety equipment.Data pro.. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D790 |
A. Schulman POLYFLAM™ E-17338 22% CACO3 Filled Copolymer Polypropylene DescriptionPolyfort® E 17338 is a 22% filled copolymer polypropylene product. Information provided by A. Schulman. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D790 |
A. Schulman POLYFLAM™ E-17338 22% CACO3 Filled Copolymer Polypropylene DescriptionPolyfort® E 17338 is a 22% filled copolymer polypropylene product. Information provided by A. Schulman. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 |
Unipetrol PP MONSTEN® EH 001 Polypropylene Homopolymer Applications include extrusions and tapes. LTHA stabilized. Homopolymer.Information provided by Unipetrol RPA |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D790 |
A. Schulman POLYFLAM™ E-17338 22% CACO3 Filled Copolymer Polypropylene DescriptionPolyfort® E 17338 is a 22% filled copolymer polypropylene product. Information provided by A. Schulman. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D790 |
Eastman Eastar CN015 Copolyester, High Flow Grade with Mold Release Applications:CompactsCosmetic jar capsCosmetic jarsCosmetics/personal care packagingFragrance capsFragrance packagingLip gloss containersLipstick containersPersonal care bottlesKey Attributes:Abilit.. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D790 |
Eastman Eastar DN011 Copolyester Eastar Copolyester DN011 is a brilliantly clear polymer having excellent impact strength, chemical resistance, and low shrinkage rates. Eastar Copolyester DN011 contains a mold release.Applications/.. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | DIN 52457 |
CP-Polymer-Technik Wellamid® 6000/42 Nylon 6, Polymer Modified, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | 0.05 in/min; ISO 178 |
CTC X-PRO TF 1113 HP Polypropylene Homopolymer, 13% Talc Filled X-PRO TF 1113 HP is a 13% talc reinforced polypropylene homopolymer, heat stabilized, and made of 98% recycled content. It has applications in: automotive under hood, IP components, fan and lightin.. |
|||
Flexural Modulus | 1.80 GPa @Temperature 23.0 °C |
261 ksi @Temperature 73.4 °F |
DAM; ISO 178 |
DuPont Performance Polymers Zytel® ST801AW BK195 Nylon 66
(Unverified Data**) Zytel® ST801AW BK195 is a Super Tough, weatherable, easy flow and processing friendly, black polyamide 66 resin for injection molding. It offers the best resistance to outdoor exposure.Information.. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D790 |
Aclo Accutech Polypropylene Homopolymer HP0334C20L1 Calcium Reinforced |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D790 |
Adell AD-10 Nylon 66, Ultra High Impact Data provided by Adell Plastics, Inc. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | DIN 52457 |
CP-Polymer-Technik Wellamid® 6000/58 CP Nylon 6, Impact Modified Until -40°C, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Flexural Modulus | 1.80 GPa @Temperature 23.0 °C |
261 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PPHC TS15020 Polypropylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 |
CENTROPLAST CENTROSOL LF Acrylonitrile butadiene Styrene copolymer conductive CENTROSOL LF ABS has high rigidity and hardness even at low temperatures. It is permanently conductive and is used in support components for the semi-conductor industry.Information provided by CENT.. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | ASTM D790 |
PlastxWorld DAICEL STYROL® GW50 HIPS UV stable flame retarded HIPSThese are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
Flexural Modulus | 1.80 GPa | 261 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Valox® VX3608C PBT (Europe-Africa-Middle East) VALOX VX3608C is an impact modified, flame retardant PBT+PC injection moulding resin. Application: electrical enclosures. This grade is 3607U with reduced oxygen index.This data was supplied by SABI.. |