Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
NYCOA 1595 HS Impact Modified, Medium Viscosity Nylon 6 Resin NYCOA 1595 HS is a medium viscosity Nylon 6 resin, which offers superior flexibility and toughness in both molding and extrusion applications. Its high melt viscosity and strength provides excellent.. |
|||
Flexural Modulus | 1.60 GPa @Temperature 23.0 °C |
232 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYfill PPC K20010 PP, 10% Mineral Reinforced Information provided by Polykemi AB |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
Shell Carilon® DP P1000 Polyketone
(discontinued **) Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON® Thermoplastic Polymer DP P1000 is the first in a family of developmental engineering polyketone resins fr.. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | Secant, 1.3 mm/min; ASTM D790 |
Phillips Sumika Marlex® CHP-370 Thermoplastic Polyolefin
(discontinued **) Thermoplastic Polyolefin, Good Stiffness and Impact PerformanceApplications: Automotive Pillar TrimConditioning after Molding: 48 hr at 23°CNominal Shrinkage: 0.8-1.0%Drying conditionsTemperature: .. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
LATI LATAN 3E71 Polyoxymethylene Copolymer (POM) with Elastomer
(Unverified Data**) Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gea.. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ISO 178 |
Total Finathene® 6006 HDPE, blow molding, pipe
(discontinued **) Finathene® 6006 is a high density polyethylene produced by the slurry loop low pressure polymerization process. Polymerization is conducted in the absence of any other comonomer. Finathene® 6006 h.. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | |
Lehmann & Voss LUVOCOM® 50-7317 Polycarbonate, with PTFE, easy flowing Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Improved friction and wear behaviour. Emergency running proper.. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | 2 mm/min; ISO 178 |
Inno-Comp INNOPOL® CS 2-9524 20% Talc-Filled, Elastomer Modified Polypropylene Block-Copolymer INNOPOL® CS 2-9524 is a 20% talc-filled, elastomer modified compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOL® CS 2-9524 is dev.. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ISO 178 |
Grupo Repol Dinalon® B1S25 DI PA6 Dry Impact Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL PPX PPX7200 PPE+PP+PS (Asia Pacific) PP+PPE+PS. Improved chemical resistance and surface aesthetics in injection molded applications. NSF61-capable. UL-94 HB listed. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics XYLEX X8210 PC+POLYESTER (Asia Pacific) PC+POLYESTER alloy. Unreinforced, transparent, impact modified for low temperature ductility |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX X8210 PC+POLYESTER (Asia Pacific) PC+POLYESTER alloy. Unreinforced, transparent, impact modified for low temperature ductility |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | 50 mm span, 5 mm/min, tangent; ASTM D790 |
A. Schulman PP 1248-01 Polypropylene High-Flow Homopolymer Polypropylene DescriptionPolypropylene PP 1248-01 is a high-flow homopolymer polypropylene nucleated and anti static designed for the high speed molding of thin-walled, multi-cavity parts. ApplicationTypical appl.. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | 2mm/min; ISO 178 |
Borealis Borcoat™ BA213E Polypropylene for Steel Pipe Coating Borcoat™ BA213E is a polypropylene compound used as a component in thermal insulation coating systems. Applications: Borcoat™ BA213E is recommended as a polymer to make foam for thermal insulatio.. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ISO 178 |
Unipetrol PP MONSTEN® GB 506 Polypropylene Impact Copolymer Applications include injection molding and thermoforming. Basic stabilization. Impact copolymer.Information provided by Unipetrol RPA |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ISO 527-2 |
Total PPH 10042 Polypropylene, Homopolymer ATOFINA Polypropylene PPH 10042 is a nucleated antistatic homopolymer. PPH 10042 is characterized by high fluidity for high speed injection of thin wall articles such as dairy pots and tubs, salad .. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ISO 178 |
Total PSI 8350 High Impact Polystyrene 8350 is a very high impact polystyrene for extrusion. This grade has an improved environmental stress crack resistance in comparison with standard high impact grades. It is proposed for the produc.. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ASTM-D790 |
Polyram RamShine PS503 Polystyrene, Flame Retardant Flame retardant, high impact polystyrene for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | dry; ISO 178 |
DSM Akulon® Fuel Lock FL-LP PA6 Low fuel permeation PA6 suitable for use in injection molding/welding of small engine fuel tanks, UV stabilized |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | cond; ISO 178 |
DSM Novamid® 3010N 5-SL4-3X NAT PA66 FR Low Viscosity, Molding Release, 30% Glass Reinforced |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | 2 mm/min; ISO 178 |
Chi Mei Polyrex® PH-60 Polystyrene - High Impact Medium impact |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
Aclo Accuguard Polypropylene HP0362V0CSL Homopolymer Flame Retardant Copper Stabilized |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
Aclo Accutech Polypropylene Homopolymer HP0336C10L1 Calcium Reinforced |
|||
Flexural Modulus | 1.60 - 13.7 GPa | 232 - 1990 ksi | Average value: 2.68 GPa Grade Count:72 |
Overview of materials for Polycarbonate, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, PTFE Filled". Each property range of values reported is minimum and maximum values of app.. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics XYLEX FXY330DF PC+POLYESTER (Asia Pacific) Polyester+PC alloy. Diffusion Effect. Color package may affect performance. |
|||
Flexural Modulus | 1.60 GPa | 232 ksi | |
Plastcom SLOVALEN PC 92 T 40 PP, 40% mineral filling FeaturesModified homopolymer and copolymer PP for injection moulding with the contenct of 40% microground, chemically modified talc. Increased strength, rigidity and thermal application up to 100°C.. |
|||
Flexural Modulus | 1.60 - 8.34266 GPa @Temperature -40.0 - 121 °C |
232 - 1210.02 ksi @Temperature -40.0 - 250 °F |
Average value: 4.93 GPa Grade Count:25 |
Overview of materials for Polypropylene with 30% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 30% Glass Fiber Filler". Specific grades with glass content between 25% and 34% are i.. |