Total PPH 10042 Polypropylene, Homopolymer

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Total Atofina
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total PPH 10042 Polypropylene, Homopolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

ATOFINA Polypropylene PPH 10042 is a nucleated antistatic homopolymer. PPH 10042 is characterized by high fluidity for high speed injection of thin wall articles such as dairy pots and tubs, salad trays and caps and closures. ApplicationPPH 10042 is nucleated and thus has improved rigidity. This coupled with a highly antistatic nature allows for shorter cycle times and easy demolding. Information provided provided by Total Petrochemicals.Total Petrochemicals acquired former Fina and Atofina plastics product lines.

Physical Properties	Metric	English	Comments
Bulk Density	0.525 g/cc	0.0190 lb/in³	ISO 1183
Density	0.905 g/cc	0.0327 lb/in³	ISO 1183
Melt Flow	35 g/10 min @Load 2.16 kg, Temperature 230 °C	35 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	98	98	ISO 2039-2
Tensile Strength, Yield	35.0 MPa	5080 psi	ISO 527-2
Elongation at Yield	8.5 %	8.5 %	ISO 527-2
Tensile Modulus	1.70 GPa	247 ksi	ISO 527-2
Flexural Modulus	1.60 GPa	232 ksi	ISO 527-2
Izod Impact, Notched (ISO)	3.00 kJ/m²	1.43 ft-lb/in²	ISO 179
Charpy Impact, Notched	0.350 J/cm²	1.67 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	165 °C	329 °F	ISO 3146
Deflection Temperature at 0.46 MPa (66 psi)	105 °C	221 °F	120°C per hour; ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi)	57.0 °C	135 °F	120°C per hour; ISO 75-2
Vicat Softening Point	90.0 °C	194 °F	50N-50°C per hour; ISO 306
	153 °C	307 °F	10N-50°C per hour; ISO 306