Inno-Comp INNOPOLÂ® CS 2-9524 20% Talc-Filled, Elastomer Modified Polypropylene Block-Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler
Manufacturer	Inno-Comp Ltd
Trade Name	INNOPOL® CS
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Inno-Comp INNOPOLÂ® CS 2-9524 20% Talc-Filled, Elastomer Modified Polypropylene Block-Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

INNOPOLÂ® CS 2-9524 is a 20% talc-filled, elastomer modified compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOLÂ® CS 2-9524 is developed for producing injection molded automotive components.All information provided by INNO-COMP.

Physical Properties	Metric	English	Comments
Density	1.03 g/cc @Temperature 23.0 Â°C	0.0372 lb/inÂ³ @Temperature 73.4 Â°F	ISO 1183
Melt Flow	28 g/10 min @Load 2.16 kg, Temperature 230 Â°C	28 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	19.0 MPa	2760 psi	50 mm/min; ISO 527-1,-2
Elongation at Yield	6.0 %	6.0 %	50 mm/min; ISO 527-1,-2
Tensile Modulus	1.50 GPa	218 ksi	1 mm/min; ISO 527-1,-2
Flexural Modulus	1.60 GPa	232 ksi	2 mm/min; ISO 178
Charpy Impact, Notched	0.450 J/cmÂ² @Temperature -20.0 Â°C	2.14 ft-lb/inÂ² @Temperature -4.00 Â°F	ISO 179/1eA
	3.00 J/cmÂ² @Temperature 23.0 Â°C	14.3 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	97.0 Â°C	207 Â°F	ISO 75-1,-2

Descriptive Properties	Value	Comments
Color	Natural