Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 1.45 GPa | 210 ksi | |
Plastcom SLOVALEN PQ 81 T 20 PP, 20% mineral filling FeaturesModified PP for injection moulding with the content of 20% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shrinkage. Gene.. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | ISO 178 |
Polimeri Europa Eraclene® MP 94 U High Density Polyethylene - Injection Molding Eraclene MP 94 U is a gas phase high density polyethylene homopolymer resin (HDPE) with antioxidants, suitable for injection molding application.This grade has a narrow molecular weight distribution.. |
|||
Flexural Modulus | >= 1.45 GPa | >= 210 ksi | ASTM D790 |
NIZHNEKAMSKNEFTEKHIM PE 2060S (60105) High Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | ISO 178 |
Polimeri Europa Eraclene® MP 90 High Density Polyethylene - Injection Molding Eraclene MP 90 is a high density polyethylene homopolymer resin (HDPE) with antioxidants, suitable for injection molding application.Eraclene MP 90 has a narrow molecular weight distribution and a h.. |
|||
Flexural Modulus | 1.45 - 115 GPa | 210 - 16700 ksi | Average value: 42.4 GPa Grade Count:7 |
Overview of materials for Epoxy Adhesive This property data is a summary of similar materials in the MatWeb database for the category "Epoxy Adhesive". Each property range of values reported is minimum and maximum values of appropriate Mat.. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | 0.05 in/min; 1% secant; Procedure A; ASTM D790 |
Phillips 66 COPYLENE® CH020 Polypropylene, Homopolymer, BOPP COPYLENE™ CH020 is a polypropylene homopolymer resin designed for BOPP (biaxially oriented polypropylene) film extrusion applications. Applications: Bags & Pouches; Raffia/Tapes/Strapping; Peelable.. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | 0.05 in/mm, 1% Secant, Procedure A; ASTM D790 |
Phillips 66 COPYLENE® CH020-03 Polypropylene, Homopolymer, BOPP COPYLENE™ CH020-03 is a polypropylene homopolymer resin designed for BOPP (biaxially oriented polypropylene) film extrusion applicationsApplications: Bags & Pouches, Raffia/Tapes/Strapping, Peelabl.. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790A |
Ineos H38G-01 Polypropylene Homopolymer, Fiber Grade
(discontinued **) Suggested fabrication methods: Fiber spinningFeatures: Very high speed spinning, Low gas fadeTypical applications: Spunbound fabricsComplies with FDA specification, Title 21, CFR 177.1520.Typical pr.. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
M. Holland Company CP501 Polypropylene Impact Copolymer AntistaticImpact copolymerHigh flowGood impact resistanceNucleatedGood stiffnessApplications: FurnitureHousehold goodsOutdoor furnishingsToys |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
Techmer ES HiFill FR® PA6/6,6 GF NAT Availability: North AmericaForms: PelletsFeatures: Flame RetardantAppearance: Natural ColorProcessing Method: Injection MoldingInformation provided by TP Composites, Inc. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | secant; ASTM D790 |
Spartech PP7130 Talc Filled High Impact Copolymer Good material choice for applications where low to medium levels of impact are required and where stiffness and heat deflection properties remain criticalInformation provided by Spartech |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP M7001XXH PP LNP* THERMOCOMP* M7001XXH is a compound based on Polypropylene resin containing proprietary antimicrobial additves. Designed for touch surfaces in patient critical healthcare applications. Added f.. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
A. Schulman PP 3486-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3486-01 is a special homopolymer polypropylene designed with long term heat aging formula for appliance application.ApplicationThis product is for injection molded applic.. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
A. Schulman PP 3489-01 Polypropylene Homopolymer DescriptionPolypropylene PP 3489-01 is a specially designed homopolymer with excellent stiffness properties. ApplicationTypical applications include high speed extrusion, high speed thin wall injec.. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1182E Talc Filled, Extrusion Grade Copolymer Polypropylene DescriptionPolyfort® FPP 1182E is a 20% talc-filled, extrusion grade copolymer polypropylene. It had a good balance of flexural modulus, low temperature impact, and appearance properties. Informat.. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
A. Schulman PP 3486-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3486-01 is a special homopolymer polypropylene designed with long term heat aging formula for appliance application.ApplicationThis product is for injection molded applic.. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | ASTM-D790 |
Polyram PlusTek PA860 Nylon 6.6, Impact Modified Super tough - impact modified polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | 1.3mm per min, 1% secant; ASTM D790 |
Formosa Plastics Formolene® 2315N Impact Copolymer Polypropylene Impact Copolymer for Injection Molding Applications Requiring Stiffness Formolene® 2315N is a high flexural modulus copolymer of polypropylene designed and formulated for injection-molded applicati.. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | 1.3mm per min, 1% secant; ASTM D790 |
Formosa Plastics Formolene® 6335N Impact Copolymer Polypropylene Impact Copolymer - Designed to Meet the Physical Requirements of Automotive Interior Trim Formolene® 6335N is an engineered, medium impact copolymer polypropylene. It was specifically developed to.. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
A. Schulman PP 1255-01 Polypropylene General Purpose Homopolymer Polypropylene DescriptionPolypropylene PP 1255-01 Natural is a general purpose molding grade, with UL 94 HB approval, homopolymer polypropylene. ApplicationPolypropylene PP 1255-01 meets FDA Regulation 21 CFR 177.. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
A. Schulman PP 3489-01 Polypropylene Homopolymer DescriptionPolypropylene PP 3489-01 is a specially designed homopolymer with excellent stiffness properties. ApplicationTypical applications include high speed extrusion, high speed thin wall injec.. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
Total PPC 4944CWZ Polypropylene, Impact Copolymer TOTAL Petrochemicals Polypropylene 4944CWZ is a nucleated and controlled rheology impact copolymer with a very high Melt Flow index of 50 g/10 min.TOTAL 4944CWZ is characterized by improved stiffnes.. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D 790 |
Total PPC 4944WZ Polypropylene, Impact Copolymer ATOFINA 4944 polypropylene is a nucleated and controlled rheology impact copolymer. 4944WZ is characterized by improved stiffness and impact resistance, as well as low shrinkage and low warpage. I.. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | ISO Data |
BASF Ultramid® HPN 9350 HS PA6 (Dry) Ultramid HPN 9350 HS is a flexible, heat stabilized, impact modified PA6 extrusion grade resin. It possesses a balance of performance properties such as good flexibility, toughness and abrasion res.. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
Carmel Olefins CAPILENE® HU 75 AV Polypropylene Impact Copolymer Description: CAPILENE® HU 75 AV is a nucleated and antistatic controlled rheology impact copolymer for injection molding. It is characterized by improved stiffness and medium impact resistance. .. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | ASTM D790 |
BCC Products BC 8165 Urethane Casting BC 8165 is a low viscosity, rapid setting, rigid urethane compound. This system will cure quickly to a hard, tough, impact resistant casting. BC 8165 is non-sensitive to moisture after cure and wil.. |
|||
Flexural Modulus | 1.45 GPa | 210 ksi | 0.05 in/min, 1% secant; ASTM D-790A |
Braskem TI4900M Impact Copolymer Polypropylene Description: Very high flexural modulus.Applications: Suggested uses include compounding, automotive interior trim, intricately designed parts, thin walled parts.Process: Injection Molding.This resi.. |