Formosa Plastics Formolene® 2315N Impact Copolymer Polypropylene

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer	Formosa Plastics Corporation, USA
Trade Name	Formolene®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Formosa Plastics Formolene® 2315N Impact Copolymer Polypropylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Impact Copolymer for Injection Molding Applications Requiring Stiffness Formolene® 2315N is a high flexural modulus copolymer of polypropylene designed and formulated for injection-molded applications. It contains a unique combination of stabilizers, nucleators and antistat that provides an excellent balance of stiffness and impact strength. Formolene® 2315N meets all requirements of the U. S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles and components of articles intended for direct food contact.Specimens were injection molded according to the conditions specified in ASTM D4101Information provided by Formosa Plastics Corporation, USA

Physical Properties	Metric	English	Comments
Density	0.900 g/cc	0.0325 lb/in³	ASTM D1505
Melt Flow	15 g/10 min @Temperature 230 °C	15 g/10 min @Temperature 446 °F	I<sub>2</sub>; ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	95	95	ASTM D785
Tensile Strength, Yield	28.3 MPa	4100 psi	2" (50mm) per min; ASTM D638
Elongation at Yield	6.0 %	6.0 %	2" (50mm) per min; ASTM D638
Flexural Modulus	1.45 GPa	210 ksi	1.3mm per min, 1% secant; ASTM D790
Izod Impact, Notched	0.641 J/cm @Temperature 0.000 °C	1.20 ft-lb/in @Temperature 32.0 °F	ASTM D256
	0.854 J/cm @Temperature 23.0 °C	1.60 ft-lb/in @Temperature 73.4 °F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	110 °C	230 °F	ASTM D648