Phillips 66 COPYLENE® CH020 Polypropylene, Homopolymer, BOPP

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Phillips 66
Trade Name	COPYLENE®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Phillips 66 COPYLENE® CH020 Polypropylene, Homopolymer, BOPP.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

COPYLENE™ CH020 is a polypropylene homopolymer resin designed for BOPP (biaxially oriented polypropylene) film extrusion applications. Applications: Bags & Pouches; Raffia/Tapes/Strapping; Peelable Film; Film Wrap; Food Packaging Film; Lamination Film; Twist Wrap Film; Surface Protection Film; Barrier Film. Equivalent to Pro-fax® HL451HInformation provided by Phillips 66.

Physical Properties	Metric	English	Comments
Density	0.902 g/cc	0.0326 lb/in³	ASTM D792
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 230 °C	2.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	33.1 MPa	4800 psi	2 in/min; ASTM D638
Elongation at Yield	12 %	12 %	ASTM D638
Flexural Modulus	1.45 GPa	210 ksi	0.05 in/min; 1% secant; Procedure A; ASTM D790
Izod Impact, Notched	0.427 J/cm @Temperature 23.0 °C	0.800 ft-lb/in @Temperature 73.4 °F	Method A; ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	93.0 °C	199 °F	unannealed; ASTM D648

Descriptive Properties	Value	Comments
Process	Film
Region	Mexico	Bamberger Polymers Distribution
	US & Canada	Bamberger Polymers Distribution