Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.950 GPa | 138 ksi | |
Plastcom SLOVALEN PQ 91T 5 PP, 5% mineral filling FeaturesModified PP for injection moulding with the content of 5 % mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shrinkage. Gene.. |
|||
Flexural Modulus | 0.950 GPa @Temperature 23.0 °C |
138 ksi @Temperature 73.4 °F |
ISO 178 |
Polykemi AB POLYten HDPE S801 HDPE, Good Abrasion Resistance, Excellent Sliding Properties Information provided by Polykemi AB |
|||
Flexural Modulus | >= 0.950 GPa | >= 138 ksi | ASTM D790 |
NIZHNEKAMSKNEFTEKHIM PP 4340S (EP2H49G) Propylene and Ethylene Copolymer Product obtained by copolymerization of propylene with ethylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation r.. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | Rotational Molded; ASTM D790 |
NOVA Chemicals Surpass® RMs244-U Octene sHDPE Rotational Molding Film Features: Octene copolymerExceptional low temperature propertiesOutstanding stiffnessBroad processing windowSuperior whiteness for improved part appearanceEasy mold releaseNSF listed for Standards 1.. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | 2% secant; ASTM D790-02 |
Ipiranga Petrochem GD 5150 K HDPE IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce .. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | ISO 178 |
Iran Petrochemical (PCC) Moplen EP-T30 U Polypropylene Moplen EP-T30 U is a heterophasic copolymer for injection moulding applications. Moplen EP-T30 U combines outstanding processability with extremely high impact Resistance. Moplen EP-T 30 U is desig.. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | 2% secant; ASTM D790-02 |
Ipiranga Petrochem GF 5150 HDPE IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce .. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP TF002 PU LNP* THERMOCOMP* TF002 is a compound based on Polyurethane resin containing 10% Glass Fiber. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | ISO 178 |
Borealis Borclear™ RD738CF Propylene Alpha Olefin Copolymer for Cast Film Borclear RD738CF is a slip and antiblock formulation propylene alpha olefin copolymer resin. It is suitable for the manufacturing of unoriented film on chill roll process.Borclear RD738CF is suitabl.. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | ISO 178 |
Borealis Borclear™ RE718CF Propylene Alpha Olefin Copolymer for Metallizable Cast Film Borclear RE718CF is a propylene alpha olefin copolymer resin formulation with antiblocking agent and without Ca-stearate, especially developed for the manufacturing of unoriented cast films for meta.. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | ISO 178 |
Unipetrol PE HD LITEN® MB/ML 77 HDPE Made for injection molding applications.Information provided by Unipetrol RPA |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | ISO 178 |
Unipetrol PP MONSTEN® GB 802 Polypropylene Random Copolymer Applications include injection molding and extrusion. Basic stabilization. Random copolymer.Information provided by Unipetrol RPA |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | Tangent; ISO 178 |
A. Schulman FORMION™ FI 393 Ionomer DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized.. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | Tangent; ISO 178 |
A. Schulman FORMION™ FI 393 Ionomer DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized.. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | ISO 178 |
Total PPC 7810 Polypropylene, Heterophasic Copolymer, High Impact Polypropylene PPC 7810 is a very high impact heterophasic copolymer with a Melt Flow index of 15 g/10 min.Polypropylene PPC 7810 has been specially developed for high impact and heavy duty applicati.. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | Tangent; ISO 178 |
A. Schulman FORMION™ FI 393 Ionomer DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized.. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | ISO 178 |
Total PPR 6280 Random Copolymer Polypropylene, Cast Film Extrusion Grade Total Petrochemicals PPR 6280 is a random copolymer polypropylene with a melt flow index of 7 g/10 min suitable for the cast extrusion of films with outstanding optical properties and easy heat weld.. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | ISO 178 |
Total PPR 6288 Random Copolymer Polypropylene, Cast Extrusion of Film Total Petrochemicals PPR 6288 is a random copolymer polypropylene with a melt flow index of 8 g/10 min for the cast extrusion of films with outstanding optical properties and easy heat weldability.P.. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | Tangent; ISO 178 |
A. Schulman FORMION™ FI 393 Ionomer DescriptionFormion® FI 393 is a 10% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low CLTE, and impact. Formion F1 393U is UV stabilized.. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | cond; ISO 178 |
DSM EcoPaXX® Q-E7300 PA410-I Tube Extrusion |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | cond; ISO 178 |
DSM EcoPaXX® Q-X07207 PA410-I Impact Modified |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | 1% secant; ASTM D790 |
Braskem CP 241 Injection Molding Polypropylene Description: CP 241 is a high melt flow rate heterophasic copolymer used for general purposes. This product offers excellent processability, easy mould filling, productivity as well as good stiffnes.. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | SAE J949 |
Azdel SuperLite® SL551000-100 PP Resin Matrix / 55% Glass Fiber (3.5 mm Molded Thickness) AZDEL SuperLite® SL551000-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | SAE J949 |
Azdel SuperLite® SL551800-100 PP Resin Matrix / 55% Glass Fiber (6 mm Molded Thickness) AZDEL SuperLite® SL551800-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | ISO 178 |
Breplast Bretene PP Polypropylene Composite Recovered polypropylene compositeInformation provided by Breplast S.p.A. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | ASTM D790 |
C.O.I.M. LARIPUR® LPR70D60 PTMG Polyether Polyurethane Description: The products of the LARIPUR® line are thermoplastic polyurethanes. These products combine the technology of thermoplastic products with the features of polyurethanes:Excellent abrasion.. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | |
Plastcom SLOVALEN PQ 83 T 10 PP, 10% mineral filling FeaturesModified PP + EPDM for injection moulding with the content of 10% mineral filler. Increased rigidity, strength and thermal. Decreased shrinkage. Application in automotive, covers of car chas.. |
|||
Flexural Modulus | 0.950 GPa | 138 ksi | ASTM D790 |
Carmel Olefins CARMELTECH™ QB 79 P Polypropylene Random Copolymer for Pressure Pipe CARMELTECH™ QB 79 P is a high molecular weight, low melt flow rate polypropylene random copolymer, especially designed for extrusion of pressure pipes and injection molding of fittings. This grade .. |