Plastcom SLOVALEN PQ 83 T 10 PP, 10% mineral filling

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVALEN
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVALEN PQ 83 T 10 PP, 10% mineral filling.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesModified PP + EPDM for injection moulding with the content of 10% mineral filler. Increased rigidity, strength and thermal. Decreased shrinkage. Application in automotive, covers of car chassis, fenders, motors, bumpers, etc.Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 0.940 g/cc
0.0340 lb/in³
Linear Mold Shrinkage 0.012 cm/cm
0.012 in/in
Linear Mold Shrinkage, Transverse 0.0124 cm/cm
0.0124 in/in
Melt Flow 12 g/10 min

@Load 0.325 kg,
Temperature 270 °C
12 g/10 min

@Load 0.716 lb,
Temperature 518 °F
Mechanical Properties Metric English Comments
Tensile Strength at Break 15.0 MPa
2180 psi
Elongation at Break 9.0 %
9.0 %
Tensile Modulus 1.20 GPa
174 ksi
Flexural Strength 18.0 MPa
2610 psi
Flexural Modulus 0.950 GPa
138 ksi
Charpy Impact Unnotched NB

@Temperature -20.0 °C
NB

@Temperature -4.00 °F
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
Charpy Impact, Notched 0.500 J/cm²

@Temperature -20.0 °C
2.38 ft-lb/in²

@Temperature -4.00 °F
4.30 J/cm²

@Temperature 23.0 °C
20.5 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 72.0 °C
162 °F
Vicat Softening Point 130 °C
266 °F
B
Processing Properties Metric English Comments
Melt Temperature 200 - 250 °C
392 - 482 °F
Mold Temperature 40.0 - 50.0 °C
104 - 122 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content <= 0.10 %
<= 0.10 %
Injection Pressure 70.0 - 120 MPa
10200 - 17400 psi