BASF Ultramid® A3HG2 10% Glass Filled PA66 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® A3HG2 10% Glass Filled PA66 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid A 3HG2 is a 10% glass fiber reinforced grade of nylon 6/6 for injection molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | dry; ISO 1183 |
| Water Absorption | 7.0 % | 7.0 % | beginning dry; ISO 62 |
| Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | beginning dry (23°C/50% R.H.); ISO 62 |
| Viscosity Test | 148 cm³/g | 148 cm³/g | Viscosity number |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM Data; MD |
| Melt Flow | 80 g/10 min @Load 5.00 kg, Temperature 275 °C |
80 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | 5mm/min; ISO 527 |
| Elongation at Break | 12 % | 12 % | 5mm/min; ISO 527 |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1mm/min; ISO 527 |
| Charpy Impact Unnotched | 9.20 J/cm² | 43.8 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | 10 K/min |
| 260 °C | 500 °F | ASTM Test |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Constant | 5.5 @Frequency 1.00e+6 Hz |
5.5 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.16 @Frequency 1.00e+6 Hz |
0.16 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- SK Chemicals SKYTHANE® U0351C Ink Binder
- Hexcel® HexPly® 913 125°C Curing Epoxy Matrix
- Toyobo Diaflora® AS 1670B
- Covestro Bayblend® FR3050 PC/ABS Blend
- Braskem LL218 Cast Film Extrusion Linear Low Density Polyethylene
- Amity Thermosets ATG 112 Phenolic Molding Organic Filler, Compression Molded
- Lubrizol ESTANE® 58224 Ester Based Thermoplastic Polyurethane
Copyright © lookpolymers.com All Rights Reserved