Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 14.0 - 30.0 MPa | 2030 - 4350 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 31008 PVDF Copolymer
(discontinued **) Key features of this grade: High Flexibility/ High Elongation/Cold Impact Resistance, Wire & Cable, Plenum, Formulated. Recommended processing is extrusion. Available as powder & granules.General .. |
|||
Tensile Strength, Ultimate | 14.0 - 30.0 MPa | 2030 - 4350 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 32008 PVDF Copolymer
(Unverified Data**) Key features of this grade: High Flexibility/ High Elongation/Cold Impact Resistance, Wire & Cable, Plenum, Formulated. Recommended processing is extrusion. Available as powder & granules.General .. |
|||
Tensile Strength, Ultimate | 21.0 - 30.0 MPa | 3050 - 4350 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 61010 PVDF Copolymer
(discontinued **) Key features of this grade: Permanent Plasticizing, Fuel Line, Piping, Formulated. Recommended processing is extrusion. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF i.. |
|||
Tensile Strength, Ultimate | 13.0 - 30.0 MPa | 1890 - 4350 psi | Average value: 20.4 MPa Grade Count:7 |
Overview of materials for Anhydride-Modified Polyethylene This property data is a summary of similar materials in the MatWeb database for the category "Anhydride-Modified Polyethylene". Each property range of values reported is minimum and maximum values o.. |
|||
Tensile Strength, Ultimate | 12.0 - 30.0 MPa | 1740 - 4350 psi | |
ATG s.r.l. IR Synthetic Polyisoprene |
|||
Tensile Strength, Ultimate | 14.0 - 30.0 MPa | 2030 - 4350 psi | |
ATG s.r.l. NR Natural Rubber |
|||
Tensile Strength, Ultimate | 25.0 - 30.0 MPa @Temperature 60.0 - 60.0 °C |
3630 - 4350 psi @Temperature 140 - 140 °F |
Average value: 28.3 MPa Grade Count:3 |
Overview of materials for Acetal Copolymer, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Glass Bead Filled". Each property range of values reported is minimum and maximum valu.. |
|||
Tensile Strength, Ultimate | 10.0 - 30.0 MPa | 1450 - 4350 psi | Average value: 22.5 MPa Grade Count:11 |
Overview of materials for Polymethylpentene, Molded This property data is a summary of similar materials in the MatWeb database for the category "Polymethylpentene, Molded". Each property range of values reported is minimum and maximum values of appr.. |
|||
Tensile Strength, Ultimate | 15.0 - 30.0 MPa | 2180 - 4350 psi | |
Hydrogenated Nitrile Rubber (HNBR) |