Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 180 MPa | 26100 psi | ASTM D638M-92 |
Propex Fabrics Curv™ C100A Polypropylene/Polypropylene Thermoformable Composite Curv™ key features include weight savings, total recyclability, no glass content, thermoformable, high impact strength, inertness, and abrasion resistance.Data provided by BP Amoco; Curv was spun o.. |
|||
Tensile Strength, Ultimate | 180 MPa | 26100 psi | ISO 527 |
LATI LARPEEK 10 G/30 30% Glass Reinforced Polyetheretherketone (PEEK)
(Unverified Data**) Larpeek polyetheretherketone (PEEK) is a high performance thermoplastic offering cost effective performance in difficult environments across all industries. PEEK is temperature resistant (up to 250°.. |
|||
Tensile Strength, Ultimate | 180 MPa | 26100 psi | ASTM D638 |
Solvay Specialty Polymers Ryton® R-4-230NA Polyphenylene Sulfide Compound
(Unverified Data**) Natural Color Polyphenylene Sulfide CompoundRyton® R-4-230NA is an advanced 40% fiberglass reinforced polyphenylene sulfide compound which provides reduced flash and improved processability compare.. |
|||
Tensile Strength, Ultimate | 180 MPa | 26100 psi | ISO 527 |
Solvay Specialty Polymers Ryton® R-4-220BL Polyphenylene Sulfide Compound
(Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-4-220BL is an advanced 40% fiberglass reinforced polyphenylene sulfide compound formulated for enhanced hydrolytic stability in applications requiring .. |
|||
Tensile Strength, Ultimate | 180 MPa | 26100 psi | ASTM D638 |
Solvay Specialty Polymers Ryton® R-4 02XT Polyphenylene Sulfide Compound
(Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-4 02XT is a 40% fiberglass reinforced polyphenylene sulfide compound that takes advantage of state-of-the-art polymerization technology to improve ducti.. |
|||
Tensile Strength, Ultimate | 180 MPa | 26100 psi | |
GBC Grade 90 Alumina Data provided by the manufacturer, GBC Materials Corporation. |
|||
Tensile Strength, Ultimate | >= 180 MPa | >= 26100 psi | |
MetalTek MTEK 78-7-15 HI LEAD Cast UNS C93800 Bearing Bronze Popular alloy with score resistance, structural uniformity, shear properties, compressive strength and low cost.Applications: Bearings, bushings, sleeves, liners, piston rings, hydraulic partsInform.. |
|||
Tensile Strength, Ultimate | 180 - 620 MPa | 26100 - 89900 psi | |
SSAB Tunnplat Docol® 420YP High-strength Steel High-strength SteelComments: Docol YP - Cold Rolled Steel - HSLA. Property values are for cold-rolled steel; thicknesses 0.5 - 3.00 mm. Iron content is approximate - exact composition is not report.. |
|||
Tensile Strength, Ultimate | 180 MPa | 26100 psi | ASTM D638 |
Chevron Phillips Xtel® XK2340 Polyphenylene Sulfide Alloy Black Polyphenylene Sulfide AlloyXtel™ XK2340 is a high performance, glass fiber reinforced, PPS-based alloy developed to provide excellent mechanical strength with an unique blend of toughness and.. |
|||
Tensile Strength, Ultimate | 180 MPa | 26100 psi | dry; ISO 527-1/-2 |
DSM Akulon® K224-G6-FC 99.99.99 PA6-GF30 30% Glass Reinforced, Food Contact Grade |
|||
Tensile Strength, Ultimate | 180 MPa | 26100 psi | dry; ISO 527-1/-2 |
DSM Akulon® K224-G6-FC BK00001 PA6-GF30 30% Glass Reinforced, Food Contact Grade |
|||
Tensile Strength, Ultimate | 180 MPa | 26100 psi | dry; ISO 527-1/-2 |
DSM Akulon® K224-G6-FC NA99001 PA6-GF30 30% Glass Reinforced, Food Contact Grade |
|||
Tensile Strength, Ultimate | 180 MPa | 26100 psi | dry; ISO 527-1/-2 |
DSM Akulon® K224-LG6 /E PA6-GF30 30% Glass Reinforced, Injection Molding, Improved UV-stability |
|||
Tensile Strength, Ultimate | 180 MPa | 26100 psi | dry; ISO 527-1/-2 |
DSM EcoPaXX® Q-X07209 PA410-I-GF40 % Glass Reinforced, Impact Modified |
|||
Tensile Strength, Ultimate | 180 MPa | 26100 psi | 5mm/min; ISO 527 |
BASF Petra® 140 45% Glass Filled PET Petra 140 is a 45% glass reinforced injection molding polyethylene terephthalate (PET) offering an increased level of strength, stiffness, high temperature performance and dimensional stability. Ex.. |
|||
Tensile Strength, Ultimate | 180 MPa | 26100 psi | 5mm/min; ISO 527 |
BASF Ultramid® 1703-2 BK ND3007 25% Glass Filled PA66 (Dry) Ultramid 1703-2 BK ND3007 is a 25% glass reinforced, heat stabilized injection molding nylon 6/6. |
|||
Tensile Strength, Ultimate | 180 MPa | 26100 psi | ATSM D638 |
Ashley Polymers Ashlene® 541-33G Nylon 66, 33% Glass Reinforced Nylon 66, 33% glass reinforced for extrusion applications.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 180 MPa | 26100 psi | dry; ISO 527-1/-2 |
DSM Stanyl® TQ261F6 PA46-GF30 30% Glass Reinforced, Heat Stabilized |
|||
Tensile Strength, Ultimate | 180 MPa | 26100 psi | dry; ISO 527-1/-2 |
DSM Stanyl® TW241F5 PA46-GF25 Heat Stabilized, 25% Glass Reinforced |
|||
Tensile Strength, Ultimate | 180 MPa | 26100 psi | cond; ISO 527-1/-2 |
DSM Novamid® MC112LG55 C10 PA6-GF55 55% Glass Reinforced |
|||
Tensile Strength, Ultimate | 180 MPa | 26100 psi | ISO 527 |
LATI LARAMID G/35 35% Glass Filled Polyphthalamide (PPA) Based Compound
(Unverified Data**) Laramid compounds are based on a unique semi-crystalline engineering polymer (polyphthalamide) offering improved performance compared to traditional engineering thermoplastics at a lower cost than s.. |