Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 170 MPa | 24700 psi | ASTM D638 |
Owens Corning Glass Fiber Reinforced Nylon 6, 30 wt.% glass Nylons, as a group, are inert to most organic solvents. They resist alkalis and salt solutions and they are attacked by strong mineral acids and oxidizing agents. Data provided by the manufacturer,.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | Same value from ASTM and ISO tests; 5 mm/min. |
BASF Capron® GR40 HS 40% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron GR40 HS is a heat stabilized 40% glass reinforced polyamide 6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensional stabil.. |
|||
Tensile Strength, Ultimate | 170.3 MPa | 24700 psi | ASTM D638 |
Plenco 50045 PET, Pellet, Injection Molded, White
(discontinued **) PLENCO 50045 is an engineering grade glass reinforced polyethylene terephthalate resin designed for higher physical strength. It is UL listed and available in white, natural, and black.Information s.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | ASTM D638 |
Solvay Specialty Polymers Amodel® AFA-6133 V0 Polyphthalamide (PPA) Resin, 33% Glass Reinforced, Dry As Molded
&nbs AMODEL AFA-6133 V0 is a 33% glass-fiber reinforced grade of polyphthalamide (PPA) resin that was developed specifically for connector applications requiring compatibility with both "infrared" and "v.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | ASTM D638 |
Solvay Specialty Polymers Ryton® R-4-200BL Polyphenylene Sulfide Compound
(Unverified Data**) Black Polyphenylene Sulfide CompoundRyton® R-4-200BL is an advanced 40% fiberglass reinforced polyphenylene sulfide compound developed to provide high strength, fast cycles, and low maintenance mol.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | ASTM D638 |
Solvay Specialty Polymers Ryton® BR42B Polyphenylene Sulfide Compound
(Unverified Data**) Natural Color Polyphenylene Sulfide CompoundRyton® BR42B is a 40% fiberglass reinforced polyphenylene sulfide compound specially formulated to have a low coefficient of friction for use in low surf.. |
|||
Tensile Strength, Ultimate | >= 170 MPa | >= 24700 psi | |
MetalTek MTEK 76-6-18 HI LEAD Cast UNS C94100 Bearing Bronze Popular alloy with score resistance, structural uniformity, shear properties, compressive strength and low cost.Applications: Bearings, bushings, sleeves, liners, piston rings, hydraulic partsInform.. |
|||
Tensile Strength, Ultimate | >= 170 MPa | >= 24700 psi | |
MetalTek MTEK 79-6-15 HI LEAD Cast UNS C93900 Bearing Bronze Popular alloy with score resistance, structural uniformity, shear properties, compressive strength and low cost.Applications: Bearings, bushings, sleeves, liners, piston rings, hydraulic partsInform.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | |
ICE Al2O3 94 Data provided by the manufacturer, International Ceramic Engineering. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | |
ICE Al2O3 96 Data provided by the manufacturer, International Ceramic Engineering. |
|||
Tensile Strength, Ultimate | 170 MPa @Temperature 982 °C |
24700 psi @Temperature 1800 °F |
|
Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Tensile Strength, Ultimate | 170 MPa @Temperature 980 °C |
24700 psi @Temperature 1800 °F |
|
Haynes 263® alloy, cold rolled sheet, solution treated and aged Very good aged strength properties, excellent fabrication characteristics when annealed, excellent intermediate temperature tensile ductility, is not normally subject to strain age cracking, excelle.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | |
Sapco 95% Aluminum Oxide Information provided by Sapco. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | ISO 527 |
Wellman Wellamid® GF33-66/6 XE-N 33% Glass Fiber Reinforced Nylon 66/6, Lubricated & Heat Stabilized Typical Applications: Machinery gear trains and linkage, conveyor belt links, fasteners, auto under hood and door parts, automotive door handles, appliance parts, sporting goods, lawn and garden equ.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | dry; ISO 527-1/-2 |
DSM EcoPaXX® Q-KG6 PA410-GF30 % Glass Reinforced, Heat Stabilized, for E&E applications |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | dry; ISO 527-1/-2 |
DSM Novamid® 1010GH30 NAT PA6-GF30 30% Glass Reinforced, Heat Stabilized, Injection Molding |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | dry; ISO 527-1/-2 |
DSM Novamid® 1013G30 1 NA PA6-GF30 30% Glass Reinforced, Injection Molding |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | dry; ISO 527-1/-2 |
DSM Novamid® 1013GH30 1 NA/BK701 PA6-GF30 30% Glass Reinforced, Heat Stabilized, Injection Molding |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | dry; ISO 527-1/-2 |
DSM Novamid® 3010GN30 NAT PA66-GF30 FR(17) 30% Glass Reinforced, Flame Retardant |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | dry; ISO 527-1/-2 |
DSM Novamid® 3021GH30 NAT PA66-GF30 30% Glass Reinforced, Heat Stabilized |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | cond; ISO 527-1/-2 |
DSM Stanyl® 46HF4550 PA46-GF50 50% Glass Reinforced, Heat Stabilized, High Flow, for E&E applications |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | cond; ISO 527-1/-2 |
DSM Stanyl® TW271B6 (PA46+PTFE)-CF30 30% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | dry; ISO 527-1/-2 |
DSM EcoPaXX® Q-HG6 PA410-GF30 30% Glass Reinforced, Heat Stabilized |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | 5mm/min; ISO 527 |
BASF Petra® 140 BK-112 45% Glass Filled PET Petra 140 BK-112 is a 45% glass reinforced, pigmented black, polyethylene terephthalate (PET) injection molding compound offering an increased level of strength, stiffness, high temperature performa.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | 5mm/min; ISO 527 |
BASF Ultramid® B3ZG7 OSI BK23273 35% Glass Filled PA6 (Dry) Ultramid B3ZG7 OSI BK23273 is a 35% glass reinforced, pigmented black, heat stabilized, impact modified PA6 injection molding grade. It was developed to meet demanding mechanical and chemical requi.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | 5mm/min; ISO 527 |
BASF Ultramid® TG7S 35% Glass Filled PA6 (Dry) Ultramid TG7S is a 34% glass reinforced, heat stabilized, impact modified PA6 injection molding grade. It was developed to meet the demanding requirements of the first North American seat
cushion .. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | dry; ISO 527-1/-2 |
DSM Novamid® 3021GH30 BK629 PA66-GF30 30% Glass Reinforced, Heat Stabilized |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | ASTM data at 5 mm/min. |
BASF Capron® 8232G HS 25% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8232G HS is a heat stabilized, 25% glass fiber reinforced nylon 6 molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. Its resista.. |
|||
Tensile Strength, Ultimate | 170 MPa | 24700 psi | Same value from ASTM and ISO tests; 5 mm/min. |
BASF Capron® GR40 40% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron GR40 is a 40% glass reinforced polyamide 6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensional stability. It is also ava.. |