Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ASTM D638 |
North Wood Plastics HDPE with 20% Wood Fiber Data provided by North Wood Plastics, Inc. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | |
3M Dyneon™ Fluorel™ FE-5620Q Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. The FE series O-ring grades are the c.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | |
3M Dyneon™ Fluorel™ FE-5621Q Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. The FE series O-ring grades are the c.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | |
3M Dyneon™ Fluorel™ FC-2182 Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. Dipolymer for autoclave curing. Used.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | |
3M Dyneon™ Fluorel™ FT-2350 Fluoroelastomer VF2 + HFP + TFE Terpolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 68.6%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. Improved retention of elongation afte.. |
|||
Tensile Strength, Ultimate | 15.0 - 60.0 MPa @Temperature 60.0 - 120 °C |
2180 - 8700 psi @Temperature 140 - 248 °F |
Average value: 36.7 MPa Grade Count:1 |
Overview of materials for Polyphenylene Ether, 10% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, 10% Glass Filled". Specific grades with glass content between 5% and 14% are includ.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ASTM D638 |
Huntsman PE 1011 Film Extrusion Polyethylene
(discontinued **) Homopolymer, Drug Master File listed product, and FDA compliant.Features: Good impact strength, good machinability, heat seal and foaming characteristicsApplications: Film Extrusion: industrial line.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ISO 527 |
LATI LATISTAT 43/7-02 Low Density Polyethylene (LDPE) Base Conductive Plastic
(discontinued **) Description: Latistat materials have low specific resistivity. They feature partial electrical conductivity. Selected functional additives give materials with low specific resistivity and reasonable.. |
|||
Tensile Strength, Ultimate | 15.0 MPa @Temperature 120 °C |
2180 psi @Temperature 248 °F |
ISO 527 |
LATI LATAMID 12 H FE90 Nylon 12 Base Magnetizable Compound
(Unverified Data**) Description: These are compounds containing a high percentage of magnetizable fillers; compared to traditional techniques for the manufacture of magnets, this allows the molding of complex shapes us.. |
|||
Tensile Strength, Ultimate | 15.0 MPa @Temperature 120 °C |
2180 psi @Temperature 248 °F |
ISO 527 |
LATI LATILUB 82-01M Nylon 12 Base, 1% Molybdenum Disulfide Self Lubricating Plastic
(discontinued **) Description: Latilub self-lubricating plastic materials are more and more often designed to replace metals in applications such as gears, bushings, cams, slides, etc), for which, besides their intri.. |
|||
Tensile Strength, Ultimate | 15.0 - 110 MPa @Temperature 60.0 - 150 °C |
2180 - 16000 psi @Temperature 140 - 302 °F |
Average value: 58.4 MPa Grade Count:4 |
Overview of materials for Nylon 12 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12". Each property range of values reported is minimum and maximum values of appropriate MatWeb en.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | |
Freudenberg Simrit V115 Standard Fluoroelastomer Excellent resistance to petroleum products and solvents. Very good high-temperature performance. Fluorocarbon elastomers make up the most widely used seals in the semiconductor industry. Avoid polar.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 330 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 335 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 330 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 335 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 330 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 330 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | at max load; ISO 527 |
A. Schulman FORMION™ FI 335 Ionomer Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | Die C (35 min / 145°C); ASTM D412 |
Dow SE BCP 817 Stereospecific high cis-1,4 Polybutadiene (BR) SE BCP 817 is manufactured by a solution process using cobalt catalyst which produces polymers with a very light color and low ash content. A non-staining stabilizer is added during the production .. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ASTM D638/D412 |
Covestro Bayflex® MP-10000 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System 0.118 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and of.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ASTM D412 |
Colorite Polymers CS6041GP Non Lead Wire and Cable Vinyl Compound Description: Colorite specialty wire and cable compounds feature low smoke properties, excellent flame retardance, low temperature flexibility, and resistance to abrasion and chemicals. All are avai.. |
|||
Tensile Strength, Ultimate | 15.0 - 35.0 MPa | 2180 - 5080 psi | |
ATG s.r.l. AU-EU Polyurethane Rubber |
|||
Tensile Strength, Ultimate | 15.0 - 20.0 MPa | 2180 - 2900 psi | |
Biomer P209 PHB Biodegradable Polymer PHB is a isotactic, absolutely linear, thermoplastic homopolyester built of 3-hydroxy butyric acid. The formula of the subunit is -[O-CH(CH3)-CH2-CO]-. PHB is free from even traces of catalysts. P.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ASTM D638 |
ExxonMobil Escorene® LD-728 High EVA Resin
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A high vinyl acetate copolymer with a low melting temperature and excellent strength properties and toughness.Applications: Injection molding; Foams.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | ASTM D638 |
Huntsman PE8010 Specialty Polyethylene
(discontinued **) Homopolymer and FDA compliant.Features: Yields film with excellent draw down and machinability.Applications: Film extrusion: gel free film applications.FDA Notes: Conforms to FDA regulation 21 CFR 1.. |
|||
Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | |
3M Dyneon™ Fluorel™ FG-5690Q Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **) Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. When compared to other food grade Dia.. |