Huntsman PE 1011 Film Extrusion Polyethylene  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman PE 1011 Film Extrusion Polyethylene  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Homopolymer, Drug Master File listed product, and FDA compliant.Features: Good impact strength, good machinability, heat seal and foaming characteristicsApplications: Film Extrusion: industrial liner/extrusion grade, drum liners, hardware packaging, automotive, and tubing.FDA Notes: Conforms to FDA regulation 21 CFR 177.1520 (c)2.2 under condition of use B through H described in Table 2 of 21 CFR 176.170Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Physical Properties Metric English Comments
Density 0.921 g/cc
0.0333 lb/in³
ASTM D1505
Thickness 25.4 microns
1.00 mil
Melt Flow 1.0 g/10 min
1.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 50
50
ASTM D2240
Tensile Strength, Ultimate 15.0 MPa
2180 psi
ASTM D638
Tensile Strength, Yield 10.0 MPa
1450 psi
ASTM D638
Film Elongation at Break, MD 325 %
325 %
ASTM D882
Film Elongation at Break, TD 425 %
425 %
ASTM D882
Elongation at Break 500 %
500 %
ASTM D638
Modulus of Elasticity 0.221 GPa
32.1 ksi
Secant; ASTM D638
Secant Modulus, MD 0.173 GPa
25.1 ksi
ASTM D882
Secant Modulus, TD 0.221 GPa
32.1 ksi
ASTM D882
Dart Drop 3.54 - 4.13 g/micron
90.0 - 105 g/mil
ASTM D1709
Dart Drop Test 90.0 - 105 g
0.198 - 0.232 lb
ASTM D1709
Film Tensile Strength at Break, TD 17.0 MPa
2470 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 91.0 °C
196 °F
ASTM D1525
Optical Properties Metric English Comments
Gloss 50 %
50 %
at 45°; ASTM D523
Processing Properties Metric English Comments
Melt Temperature 171 - 182 °C
340 - 360 °F