3M Dyneon™ Fluorel™ FE-5621Q Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | 3M Dyneon™ Fluorel™ FE-5621Q Fluoroelastomer VF2 + HFP Dipolymer
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, Dyneon LLC.Incorporated cure polymer, 65.9%F in polymer with 22% Medium Thermal Carbon Black (N990), 2% MgO, and 4% Ca(OH)2. The FE series O-ring grades are the cleanest running Dyneon O-ring grade polymers available; provide excellent mold release & improved scorch safety. This allows molding at higher temperatures (>200°C) for faster cure cycles - resulting in parts with improved dimensional stability. FE-5621Q and FE-5641Q have lower mold shrinkage. Used in O-Ring Applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | |
| Oxygen Transmission | 98.0 cc-mm/m²-24hr-atm | 249 cc-mil/100 in²-24hr-atm | |
| Mooney Viscosity | 23 @Temperature 121 °C |
23 @Temperature 250 °F |
ML1+10 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 77 | 77 | |
| Tensile Strength, Ultimate | 15.0 MPa | 2180 psi | |
| Tensile Strength, Yield | 6.60 MPa | 957 psi | M100 |
| Elongation at Break | 195 % | 195 % | |
| Coefficient of Friction, Dynamic | 0.80 | 0.80 | |
| Compression Set | 13 % @Temperature 200 °C |
13 % @Temperature 392 °F |
70 hr; ASTM D395B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 200 µm/m-°C @Temperature 20.0 °C |
111 µin/in-°F @Temperature 68.0 °F |
|
| Specific Heat Capacity | 1.65 J/g-°C | 0.394 BTU/lb-°F | |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | |
| Glass Transition Temp, Tg | -18.0 °C | -0.400 °F | TR10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+13 - 1.00e+14 ohm-cm | 1.00e+13 - 1.00e+14 ohm-cm | |
| Dielectric Constant | 11.4 @Frequency 6.00e+7 Hz |
11.4 @Frequency 6.00e+7 Hz |
|
| Dielectric Strength | 25.0 kV/mm | 635 kV/in |
Users viewing this material also viewed the following:
- MV Labs YB870 Yb2(C2O4)3·10H2O Ytterbium oxalate hydrate
- NeXolve UV Blocking Optionox® Polyimide Film/Coating
- Hong Kun Group D-Homoproline Methyl Ester Hydrochloride Pharmaceutical Intermediate
- Lucite International Diakon® TD525 Toughened Acrylic Compound
- LATI Latamid 66 LH2 G/35 PA 66, 35% Glass Fiber Reinforced, Heat Stabilized
- Shandong Rike Chemical HELIâ„¢ HG-400 PVC Processing Aid Series (PA)
- EMS-Griltech Griltex® 9E Copolyester Hotmelt Adhesive (Apparel Interlinings)
- Ensinger TECASINT 4201 SD Polyimide, Black, Carbon Fiber (PI)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 4.0 PHR MBT
Copyright © lookpolymers.com All Rights Reserved