Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 77.2 - 234 MPa | 11200 - 34000 psi | Average value: 175 MPa Grade Count:12 |
Overview of materials for Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler". Specific grades with carbon fiber content bet.. |
|||
Tensile Strength, Ultimate | 77.0 - 281.306 MPa @Temperature -40.0 - 150 °C |
11200 - 40800.1 psi @Temperature -40.0 - 302 °F |
Average value: 104 MPa Grade Count:4 |
Overview of materials for Nylon 6, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. E.. |
|||
Tensile Strength, Ultimate | 76.9 MPa | 11200 psi | |
MMCC Aluminum/Graphite Fiber GA 7-230 Metal Matrix Composite Discontinuous graphite fiber aluminum product primarily used for electronic thermal management applications. Lightweight, high damping, stiffer than aluminum, matched cte, easily machined and plate.. |
|||
Tensile Strength, Ultimate | 77.0 MPa @Temperature 1095 °C |
11200 psi @Temperature 2003 °F |
|
Haynes 718 alloy, cold rolled, solution-treated and aged sheet Cb and Ta content combined weight percentage of 5. Excellent high-temperature strength up to 650°C, good ductility, formability, and weldability. Very good welding characteristics. Applications i.. |
|||
Tensile Strength, Ultimate | 77.0 MPa | 11200 psi | ISO 527-1, 2 |
Polyplastics Duranex® CTN7133 Polybutylene Terephthalate (PBT), Higher comparative tracking index, FR, GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Tensile Strength, Ultimate | 77.0 MPa | 11200 psi | ISO 527-2/1A/5 |
Lubrizol ESTALOC® T5160 Ether-Type, Reinforced Engineering Thermoplastic (European Grade) Description: Estaloc® RETP (Reinforced Engineering Thermoplastic) is a tough, dimensionally stable, abrasion-resistant thermoplastic that withstands demanding environments. Developed as an extensio.. |
|||
Tensile Strength, Ultimate | 77.0 MPa | 11200 psi | dry; ISO 527-1/-2 |
DSM Novamid® 1010GN7-20 BK37 PA6-GF20 FR(30) 0 20% Glass Reinforced, Flame Retardant, Halogen free |
|||
Tensile Strength, Ultimate | 77.2 MPa | 11200 psi | |
BCC Products BC 5003 Epoxy Laminating System BC 5003 is a medium viscosity, unfilled laminating system. It is a room temperature curing resin with a relatively short pot life. BC 5003 is also considered an excellent general purpose adhesive fo.. |
|||
Tensile Strength, Ultimate | 77.0 MPa | 11200 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 113 Polypropylene, Glass Reinforced, Chemically Coupled Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 77.0 MPa | 11200 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 249 SAN, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 77.0 MPa | 11200 psi | ASTM D638 |
A. Schulman ComAlloy Hiloy® 262 Glass Reinforced, Modified SMA Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 77.0 MPa | 11200 psi | ASTM D638 |
Aardvark Polymers Aarlon® 2000 Rotational Molding Resin, 50% RH Aarlon® 2000 PA 6/6 is a high performance nylon for rotational molding applications. Aarlon® 2000 offers high heat capabilities with exceptional mechanical properties.Information provided by Gehri.. |
|||
Tensile Strength, Ultimate | 77.0 MPa | 11200 psi | ASTM D638 |
Plenco 1510 Polyester, Granular, Transfer Molded PLENCO 01510 is a mineral filled, pelletized polyester molding compound, which offers an excellent combination of electrical properties and dimensional stability. UL recognized under component file .. |
|||
Tensile Strength, Ultimate | 77.0 MPa | 11200 psi | ASTM D638 |
Plenco 1581 Polyester, Briquette, Transfer Molded PLENCO 01581 is a glass and mineral reinforced pelletized polyester molding compound, exhibiting excellent dimensional stability, mechanical strength and also arc resistance, track resistance, and f.. |
|||
Tensile Strength, Ultimate | 77.22 MPa | 11200 psi | |
Phenolic 30%, Graphite fabric 70% Phenyl silane - C.T.L "37-9X". Graphite fabric - "WCB" |