- A. Schulman ComAlloy Hiloy® 249 SAN, Glass Reinforced
A. Schulman ComAlloy Hiloy® 249 SAN, Glass Reinforced
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded, Glass Reinforced |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Hiloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Hiloy® 249 SAN, Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Ultimate | 77.0 MPa | 11200 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 112 MPa | 16200 psi | ASTM D790 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ASTM D790 |
| Izod Impact, Notched | 0.430 J/cm | 0.806 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.33 J/cm | 2.49 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 235 - 266 °C | 455 - 511 °F |
Users viewing this material also viewed the following:
- BASF Capron® HPN 9333G Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned) (discontinued **)
- Plenco 201 Black General Purpose Woodflour/Mineral Filled Phenolic Molding Compound (discontinued **)
- H.C. Starck Amperit® 559.074 Agglomerated, Sintered Tungsten Carbide-Cobalt-Chromium 86-6-8 (WC-Co-Cr)
- DuPont Elvanol® 50-26 Polyvinyl Alcohol Partially Hydrolyzed General Purpose Grade
- ExxonMobil HDPE HTA 108 High Density Polyethylene Resin
- Diamond Polymers ASA M-143
- Alliance C-5 Strontium Ferrite Ceramic Magnetic Material
- Aremco AREMCOLOX™ 502-1100 (Full-Fired) Dense Alumino-Silicate
- DuPont™ Kapton® 200VN Polyimide Film, 50 Micron Thickness
Copyright © lookpolymers.com All Rights Reserved