A. Schulman ComAlloy Hiloy® 113 Polypropylene, Glass Reinforced, Chemically Coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Hiloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Hiloy® 113 Polypropylene, Glass Reinforced, Chemically Coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 103 | 103 | ASTM D785 |
| Tensile Strength, Ultimate | 77.0 MPa | 11200 psi | ASTM D638 |
| Elongation at Break | 1.3 % | 1.3 % | ASTM D638 |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 5.90 GPa | 856 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.50 J/cm | 10.3 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 161 °C | 322 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 229 - 246 °C | 444 - 475 °F |
Users viewing this material also viewed the following:
- Polimeri Europa Clearflex® FG 368 Octene Comonomer Linear Low Density Polyethylene
- Polymer Resources AH-GP3 Acetal Homopolymer, High Flow Resin, Heat Stabilized
- PB1100-55 Polyurethane-based Biomedical Elastomer
- Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 40% Glass Fiber Filled
- Akro-Plastic Akromid® B3 S3 75 PA, Dry-Impact Resistant (discontinued **)
- Materion BrushBronze® 95510 (AMS 4880) Centrifugal Cast 1.0" - 17.0"
- Sumitomo Chemical ESPOLEX® WT485 Thermoplastic Elastomer
- A. Schulman POLYBATCH™ White L8350 HSF Concentrate Based In High-Flow LLDPE
- Eagle Brass 260 Cartridge Brass, 3/4 Hard
- Arlon 10502R030 0.040" (1.02 mm) Cured/Post-Cured Unsupported Silicone Rubber
Copyright © lookpolymers.com All Rights Reserved