Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
Nylene® Naxel™ A914 Polycarbonate/ABS Alloy Description: Naxel™ A914 is a Polycarbonate/ABS alloy. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ISO 527 |
LATI LASTANE 50 G/25 25% Glass Fiber Reinforced Polyurethane (PUR)
(Unverified Data**) Description: Lastane thermoplastics are polyurethane (PUR) products. They exhibit good wear and impact resistance, even at low temperatures, noise inertness and excellent mould release. These proper.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D882 |
SABIC Innovative Plastics Lexan® FR60 Polycarbonate Film, Flame Retardant Lexan FR60 flame-retardant film is a clear, thin-gauge polycarbonate film with polished surfaces on both sides, and a UL94 V-0 listing to meet the stringent requirements in a wide range of electrica.. |
|||
Tensile Strength, Ultimate | 60.0 MPa @Temperature 60.0 °C |
8700 psi @Temperature 140 °F |
ISO 527 |
LATI LATAN 13 G/303 30% Glass Fiber Reinforced Polyoxymethylene Copolymer (POM)
(discontinued **) Description: Latan series thermoplastics are polyoxymethylene copolymer (POM) products. The main applications for Latan feature good wear resistance, chemical inertness and low water absorption (gea.. |
|||
Tensile Strength, Ultimate | 60.0 - 145 MPa @Temperature 60.0 - 150 °C |
8700 - 21000 psi @Temperature 140 - 302 °F |
Average value: 108 MPa Grade Count:3 |
Overview of materials for Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled". Each property range of values reported is mini.. |
|||
Tensile Strength, Ultimate | 60.0 - 105 MPa | 8700 - 15200 psi | Average value: 84.8 MPa Grade Count:3 |
Overview of materials for Nylon 66/6, 10% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% are incl.. |
|||
Tensile Strength, Ultimate | 60.0 - 140 MPa @Temperature 60.0 - 150 °C |
8700 - 20300 psi @Temperature 140 - 302 °F |
Average value: 95.6 MPa Grade Count:2 |
Overview of materials for Nylon 612, Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Glass Fiber Filler". Each property range of values reported is minimum and maximum values of .. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | DIN 53455; ASTM D638 |
Kolon NOPLA® KE831 PEN-PET Copolyester NOPLA® is an advanced PEN-PET copolyester which can be used for bottle, sheet & injection molding applicationsUV protection & prolonged outdoor durability, enhanced gas barrier, outstanding impac.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
LG Chemical Lupoy 1621-02 Polycarbonate Resin Description: LUPOY PC 1621-02 resin is designed for large injection stretch blow molding and extrusion blow molding parts. It exhibits an excellent physical property balance of heat resistance, tran.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
LG Chemical Lupoy 3010-10 Polycarbonate Resin Description: LUPOY PC 3010-10 resin is designed for injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.Main Character.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
LG Chemical Lupoy 3030-10 Polycarbonate Resin Description: LUPOY PC 3030-10 resin is designed for injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.Main Character.. |
|||
Tensile Strength, Ultimate | 60.0 MPa @Temperature 22.0 °C |
8700 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® SMC 0200 Unsaturated Polyester UP SMC 0200 is a general purpose SMC for a wide range of applications. Typically, it is used as housings, covers and functional components in mechanical engineering. The flammability meets the demands .. |
|||
Tensile Strength, Ultimate | 60.0 MPa @Temperature 22.0 °C |
8700 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® SMC 1000 Unsaturated Polyester UP SMC 1000 is a special SMC for hydrolysis resistant applications. The glass level has been selected to combine good mouldability with good strength and stiffness properties. Typical applications are .. |
|||
Tensile Strength, Ultimate | 60.0 MPa @Temperature 22.0 °C |
8700 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® SMC 0290 Unsaturated Polyester UP SMC 0290 is a specially formulated SMC processable by injection moulding. The gentle production process prevents the fiber from any damage. Parts made of SMC 0290 reach higher levels of strength and.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
LG Chemical Lupoy 3010-30 Polycarbonate Resin Description: LUPOY PC 3010-30 resin is designed for injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.Main Character.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | |
Saint-Gobain Micaver® Glass-Mica Electrical Insulator, Compression Moldings Glass-mica compound that occupies a place between plastics and ceramics in terms of usage temperature. It can be molded and machined like plastics and has the mechanical properties (strength, hardn.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
Plenco 00757 Melamine-Phenolic, Granular, Injection Molded PLENCO 00757 is a melamine-phenolic, copolymer molding compound, offering excellent arc resistance and comparative track index values. It is formulated to provide improved mechanical strength proper.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ISO 527-1, 2 |
Polyplastics Duranex® 2002U Polybutylene Terephthalate (PBT), Weather resistance DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers .. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D882 |
Chengdu Polyster KLX-G11 PC Film & Sheet PC film and sheet, high transparency, both sides are polished, both sides with transparent protective films. Is printable, flame-retardant, anti-static, resists ultraviolet decay, scratch resistant,.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
Covestro Makrolon® 2205 Polycarbonate, Injection Grade Exceptionally good flow injection molding grade with easy mold release, for parts with a low wall thickness and long flow paths.Information provided by Bayer.As of 1 September 2015, Bayer MaterialSc.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | |
Covestro Makrolon® 8025 Polycarbonate High viscosity extrusion and injection molding grade with 20% short glass fibers and easy mold release, low anisotropy, for stiff moldings requiring good dimensional stability.Information provided b.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ATSM D638 |
Ashley Polymers Ashlene® 745 Nylon 6/69 A special copolymer ideal for blown and cast film coextrusion. This is a gel free resin with outstanding lot to lot consistency being produced by a continuous process. It has a lower melting point.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | 5mm/min; ISO 527 |
BASF Ultramid® B3ZG3 15% Glass Filled PA6 (Conditioned) Ultramid B3ZG3 is an impact-modified, 15% glass fiber reinforced injection molding PA6 grade. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ATSM D638 |
Ashley Polymers Ashlene® 180 Acetal A general purpose, high viscosity, natural.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 60.0 - 150 MPa @Temperature 120 - 200 °C |
8700 - 21800 psi @Temperature 248 - 392 °F |
Average value: 103 MPa Grade Count:7 |
Overview of materials for Nylon 46, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Glass Fiber Reinforced". Each property range of values reported is minimum and maximum values .. |
|||
Tensile Strength, Ultimate | 60.0 - 75.0 MPa @Temperature 130 - 175 °C |
8700 - 10900 psi @Temperature 266 - 347 °F |
Average value: 69.4 MPa Grade Count:2 |
Overview of materials for Nylon 6, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Glass Fiber Filled".Specific grades with glass content between 15% and 24% are included. Ea.. |
|||
Tensile Strength, Ultimate | 60.0 - 75.0 MPa @Time 1.80e+7 - 7.20e+7 sec |
8700 - 10900 psi @Time 5000 - 20000 hour |
Average value: 69.4 MPa Grade Count:2 |
Overview of materials for Nylon 6, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Glass Fiber Filled".Specific grades with glass content between 15% and 24% are included. Ea.. |
|||
Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ATSM D638 |
Ashley Polymers Ashlene® P1053R Polycarbonate A high flow transparent polycarbonate with good impact properties containing UV stabilizer.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 60.0 - 150 MPa @Temperature 60.0 - 230 °C |
8700 - 21800 psi @Temperature 140 - 446 °F |
Average value: 100 MPa Grade Count:8 |
Overview of materials for Polyphthalamide (PPA), 30% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 30% Glass Fiber Reinforced". Specific grades with glass content between 25% and 34% are.. |