- Polymer Property : Tensile Strength, Ultimate = 25.0 MPa
Polymer Property : Tensile Strength, Ultimate = 25.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | ASTM D638 |
| NCMT NanoPAC™ N10 High Performance Polypropylene Nanocomposite Characteristics: Less shrinkage Solved distortion problem Good balance in impact and stiffness High gloss Reduce production cycleApplications: Household Industry Electrical Appliances Toys IndustryI.. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | ASTM D638 |
| North Wood Plastics Polypropylene with 20% Wood Fiber, Molding Grade Data provided by North Wood Plastics, Inc. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | ASTM Data |
| Americas Styrenics Styron® 8100 MFD High Impact Polystyrene
(discontinued **) STYRON 8100 MFD high impact polystyrene is designed for microfloppy diskettes (MFD) applications. It offers easy processing, coloring, abrasion resistance, impact strength, and high heat resistance... |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | ASTM D638 |
| Total Finaclear® 530 Clear Impact Polystyrene
(discontinued **) Finaclear® 530 is a clear high styrenic styrene-butadiene (SBS) elastomer, providing dramatically improved impact properties and tear resistance to finished articles, when used in blends with other.. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | DIN 53455 |
| Ineos Nova S-3400 Medium Impact Compact Polystyrene
(discontinued **) Impact polystyrene with good flow characteristics and a high elongation. Generally used for applications where a tough material is required. For injection molding generally a lubricated type is us.. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | DIN 53455 |
| Ineos Nova S-3401 Medium Impact Compact Polystyrene
(discontinued **) Impact polystyrene with good flow characteristics and a high elongation. Generally used for applications where a tough material is required. The material is provided with external lubricate to imp.. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | DIN 53455 |
| Ineos Nova S-6600 High Impact Compact Polystyrene
(discontinued **) High impact polystyrene which is very easy processed in extension and thermoforming processes. Typical applications are packaging of food stuffs like Yot beakers but technical parts and extruded pr.. |
|||
| Tensile Strength, Ultimate | 25.0 - 85.0 MPa @Temperature 60.0 - 120 °C |
3630 - 12300 psi @Temperature 140 - 248 °F |
Average value: 60.0 MPa Grade Count:2 |
| Overview of materials for Polycarbonate, Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Glass Fiber Filled, Flame Retardant". Each property range of values reported is minimum a.. |
|||
| Tensile Strength, Ultimate | 25.0 - 45.0 MPa | 3630 - 6530 psi | 50 mm/min; ASTM D638 |
| Solvay Specialty Polymers Solef® 1015/0078 PVDF Homopolymer
(discontinued **) Key features of this grade: Plasticized, Offshore, Piping, Formulated. Recommended processing is extrusion. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorina.. |
|||
| Tensile Strength, Ultimate | 25.0 - 178 MPa @Temperature -40.0 - 150 °C |
3630 - 25800 psi @Temperature -40.0 - 302 °F |
Average value: 66.1 MPa Grade Count:9 |
| Overview of materials for Nylon 6, Glass/Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Glass/Mineral Reinforced". Each property range of values reported is minimum and maximum values.. |
|||
| Tensile Strength, Ultimate | 25.0 - 55.0 MPa @Temperature 60.0 - 150 °C |
3630 - 7980 psi @Temperature 140 - 302 °F |
Average value: 38.4 MPa Grade Count:2 |
| Overview of materials for Nylon 66, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Bead Filled". Each property range of values reported is minimum and maximum values of ap.. |
|||
| Tensile Strength, Ultimate | 25.0 - 215 MPa @Strain 1.00 - 10.0 % |
3630 - 31200 psi @Strain 1.00 - 10.0 % |
Average value: 88.6 MPa Grade Count:5 |
| Overview of materials for Nylon 66, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
| Tensile Strength, Ultimate | 25.0 - 215 MPa @Temperature -40.0 - 150 °C |
3630 - 31200 psi @Temperature -40.0 - 302 °F |
Average value: 88.6 MPa Grade Count:5 |
| Overview of materials for Nylon 66, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
| Tensile Strength, Ultimate | 25.0 - 400 MPa @Strain 1.00 - 10.0 % |
3630 - 58000 psi @Strain 1.00 - 10.0 % |
Average value: 101 MPa Grade Count:5 |
| Overview of materials for Nylon 66, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. .. |
|||
| Tensile Strength, Ultimate | 25.0 - 195 MPa @Temperature 60.0 - 120 °C |
3630 - 28300 psi @Temperature 140 - 248 °F |
Average value: 128 MPa Grade Count:1 |
| Overview of materials for Nylon 66, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. .. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | |
| Kuraray HYBRAR® HD3 Thermoplastic Rubber-HDPE Blend Description: HYBRAR® is another in the series of new high performance thermoplastic rubbers developed by KURARAY using their unique isoprene technology. HYBRAR® is a special thermoplastic rubb.. |
|||
| Tensile Strength, Ultimate | 25.0 MPa @Temperature 22.0 °C |
3630 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Menzolit Menzolit® BMC 3100 Unsaturated Polyester UP BMC 3100 is a special BMC suitable for the use in head lamp reflectors. Because of its high temperature resistance and dimensional stability as well as low coefficient of thermal expansion, complex .. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | ASTM D638 |
| LyondellBasell Astryn BB724AC Polypropylene Copolymer Key Features: medium high melt flow, high modulus, mineral-filled polypropylene copolymer, high rigidity, good impact resistance, good processabilityApplications: automotive heater and A/C ductworkD.. |
|||
| Tensile Strength, Ultimate | 25.0 - 34.0 MPa | 3630 - 4930 psi | |
| Cosmic Plastics 306 Orlon Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | at max load; ISO 527 |
| A. Schulman FORMION™ FI 394 Ionomer Information provided by A. Schulman. |
|||
| Tensile Strength, Ultimate | 25.0 MPa @Temperature 80.0 °C |
3630 psi @Temperature 176 °F |
ASTM D638 |
| Toyobo NB-5620S Nylon/Olefin Alloy, 15% Mineral Reinforced (DAM) Features: 15% Mineral Reinforced, Light WeightInformation provided by Toyobo. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | at max load; ISO 527 |
| A. Schulman FORMION™ FI 394 Ionomer Information provided by A. Schulman. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | ASTM D638 |
| A. Schulman ComAlloy Comtuf® 164 Polypropylene, Mineral Reinforced, Chemically Coupled, Impact Modified Data provided by the manufacturer, ComAlloy International Company.20% Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been i.. |
|||
| Tensile Strength, Ultimate | 25.0 - 215 MPa @Temperature -55.0 - 275 °C |
3630 - 31200 psi @Temperature -67.0 - 527 °F |
Average value: 109 MPa Grade Count:18 |
| Overview of materials for Polyetheretherketone, Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetheretherketone, Glass Fiber Filled". Each property range of values reported is minimum and maximum.. |
|||
| Tensile Strength, Ultimate | 25.0 MPa @Temperature 60.0 °C |
3630 psi @Temperature 140 °F |
ISO 527 |
| LATI LASTIROL TR G/10-V1 10% Glass Fiber Reinforced Polystyrene (PS) (UL94 V-1)
(discontinued **) Description: Lastirol thermoplastics are polystyrene (PS) products. The Lastirols feature excellent dimensional stability, good flowability, and can be molded without any particular problem. Glass f.. |
|||
| Tensile Strength, Ultimate | 25.0 MPa | 3630 psi | at max load; ISO 527 |
| A. Schulman FORMION™ FI 394 Ionomer Information provided by A. Schulman. |
|||
| Tensile Strength, Ultimate | 25.0 - 325 MPa | 3630 - 47100 psi | Average value: 114 MPa Grade Count:222 |
| Overview of materials for Polyethersulfone (PES) This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
| Tensile Strength, Ultimate | >= 25.0 MPa | >= 3630 psi | ASTM D638 |
| Borealis Borstar® HE6062 HDPE Black Jacketing Compound Borstar HE6062 is a black, bimodal co-polymer high density polyethylene (HDPE) compound produced using the Borealis Borstar process. It is characterized by balanced properties important in jacketin.. |
|||