Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | ASTM D638 |
Multibase Multi-Pro® 5012 C Natural Polypropylene Forms:PelletsProcessing Methods:Injection MoldingFeatures:Gloss, LowInformation provided by Multibase |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | Mixed 1:2; TM R050-36 |
Resinlab® EP1215 Clear Unfilled Epoxy Structural Adhesive Resinlab™ EP1215 Clear is a two part unfilled epoxy structural adhesive designed for bonding applications requiring high strength and good impact resistance. It cures completely at room temperature.. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | TM R050-36 |
Resinlab® EP1287 Filled, Flame Retardant Epoxy Syntactic Foam Resinlab™ EP1287 is a two part filled, flame retardant epoxy syntactic foam. It utilizes glass microspheres to reduce cured density and improve machinability. This product will be self-extinguishin.. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | 500 mm/min (20 in./min.); ASTM D638, Type IV Specimen |
Eastman 1810A Polyethylene
(discontinued **) Polyethylene 1810A contains no additives. It is suggested for injection molding applications.Information from manufacturer data sheet.Eastman Chemical Company sold its polyethylene business to West.. |
|||
Tensile Strength, Ultimate | 13.8 - 85.0 MPa | 2000 - 12300 psi | Average value: 62.3 MPa Grade Count:11 |
Overview of materials for Epoxy, High Temperature This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Encapsulating, Mineral Filled". Each property range of values reported is minimum and maximum val.. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | ASTM D3574E |
Mearthane Durethaneâ„¢ F DF-235A Closed Cell Foam Polyurethane TDI backbone: ester.Shore 00 Hardness: 80Summary: Durethane F is chemically blown urethane closed cell foam. Mearthane can custom formulate Durethane F, varying the physical properties (coefficient.. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | |
Sylvin Technologies 8915-70 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | |
Sylvin Technologies 8940-75 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | |
Sylvin Technologies 9915-70 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | |
Sylvin Technologies 9940-75 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | |
Sylvin Technologies 9950-95 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | ASTM D412 |
Lubrizol Estane® ZHF 95AT3 Thermoplastic Polyurethane, Flame Retardant Type: Estane® ZHF 95AT3 TPU is a zero halogen flame retardant polyether based thermoplastic polyurethane compound.Features: Outstanding flame retardant properties, especially suited for tray cables.. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | ASTM D638 |
Chevron Phillips MarFlex® 1017 General Purpose Coating Resin Characteristics: Excellent Processability, High Temperature Stability, Low Neck-inApplications:Flexible Packaging, Laminations, Sealant Resin, General Purpose Coating ResinData provided by Chevron C.. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | ASTM D638 |
Ecomass® 4703ZD95 Tungsten Filled Polyurethane Nontoxic alternative to Lead (Pb), weighting, balancing and radiation shielding applicationsHigh Specific GravityTungsten Powder Filled Polyurethane (TPU)FlexibleInformation provided by Technical Po.. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | ASTM D638 |
Chevron Phillips Marlex® 1007 Injection Molding Resin Resin Type: Homopolymer; ASTM D 4976 Classification: PE 113, A 25200Characteristics: Excellent Flexibility, Good Flow, Good Warping Resistance, Moderate Mold Release, Good ESCRApplications:Houseware.. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | ASTM D638 |
Chevron Phillips Marlex® 1122B Injection Molding Resin Resin Type: Homopolymer; ASTM D 4976 Classification: PE 113, A 24200Characteristics: Excellent Flexibility, Moderate Flow, Moderate Warping Resistance, Moderate Mold Release, Excellent ESCRApplicati.. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | |
Cytec EN-2555 (Conap) Potting and Encapsulation Adhesive Polyurethane Potting and Encapsulating SystemsConathane® EN-2500 series polyurethane potting and encapsulating systems from Cytek have varying degrees of worklife, viscosity and hardness for many s.. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | ASTM D638 |
Dow AMPLIFY™ GR 209 Maleic anhydride grafted (MAH) polymer AMPLIFY™ GR 209 Functional Polymer is a post reactor maliec anhydride grafted (MAH) polymer. The base polymer is an ethylene-butene copolymer exhibiting high flexibility and elasticity. It can be.. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | ASTM D638 |
Colorite Polymers 7284 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | |
Dymax 950 Potting and Encapsulation Adhesive High Performance Light-Curing Adhesives and Coatings for Electronic AssemblyDymax 950 Potting and Encapsulation AdhesiveSuperior bonds to glass and epoxy board excellent moisture resistance, deep cu.. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | ASTM D638 |
Colorite Polymers 6588 Non-Phthalate 88 Series Vinyl Compound Description: The Colorite 88 series is a family of vinyl non-toxic compounds formulated to provide excellent low temperature flexibility characteristics. These compounds are designed for outside doo.. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | ASTM D638 |
Colorite Polymers 6800-UV General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | |
Colorite Polymers 7012 Clear Injection Molding Vinyl Compound Description: Clear non-toxic vinyl compounds are utilized by the health and medical industries for injection molding of various components such as drip chambers, connectors, valves, etc. The vinyl c.. |
|||
Tensile Strength, Ultimate | 13.8 - 300 MPa | 2000 - 43500 psi | Average value: 89.6 MPa Grade Count:23 |
Overview of materials for Epoxy Molding Compound This property data is a summary of similar materials in the MatWeb database for the category "Epoxy Molding Compound". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Tensile Strength, Ultimate | 13.8 MPa | 2000 psi | |
Sylvin Technologies 6150-80 PVC Wire/Cable Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 13.8 - 180 MPa | 2000 - 26100 psi | Average value: 105 MPa Grade Count:277 |
Overview of materials for Nylon 6, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Glass Fiber Filled".Specific grades with glass content between 15% and 24% are included. Ea.. |